• W4386204408 abstract "Factors that promote hydrogen-related intergranular (IG) fracture in the elastic region of tempered martensitic steel have been identified utilizing frozen-in hydrogen distribution and tensile tests in liquid nitrogen at -196°C. Tensile test results at room temperature (R.T.) after precharging with 12.1 mass ppm of hydrogen showed hydrogen embrittlement associated with IG fracture. Although tensile test results at -196°C after precharging with the same amount of hydrogen did not show hydrogen embrittlement with IG fracture, those at -196°C after preloading with elastic stress just before fracture strength at R.T. showed hydrogen embrittlement with IG fracture. As preloading stresses increased and preloading speeds decreased, subsequent hydrogen embrittlement susceptibility at -196°C increased. In addition, although tensile testing at -196°C after hydrogen precharging, preloading at R.T., and unloading at -196°C resulted in IG fracture, testing conducted after unloading at R.T. did not. It is noted that reversible hydrogen that accumulates on prior austenite grain boundaries (PAGBs) in the presence of load and desorbs in the absence of load in the elastic region at R.T. is directly responsible for IG fracture. These findings revealed that hydrogen-related IG fracture in the elastic region of tempered martensitic steel was not caused by stress-free hydrogen distribution, but was promoted by reversibly accumulated hydrogen mainly due to stress-induced diffusion onto PAGBs during stress loading at R.T." @default.
• W4386204408 created "2023-08-28" @default.
• W4386204408 creator A5020823658 @default.
• W4386204408 creator A5074573081 @default.
• W4386204408 date "2023-10-01" @default.
• W4386204408 modified "2023-09-24" @default.
• W4386204408 title "Extraction of reversible hydrogen trapped on prior austenite grain boundaries and promoting intergranular fracture in the elastic region of tempered martensitic steel by utilizing frozen-in hydrogen distribution at -196°C" @default.
• W4386204408 cites W1978667625 @default.
• W4386204408 cites W1988545792 @default.
• W4386204408 cites W1993956200 @default.
• W4386204408 cites W1995971143 @default.
• W4386204408 cites W2001779076 @default.
• W4386204408 cites W2013980730 @default.
• W4386204408 cites W2032398648 @default.
• W4386204408 cites W2035850367 @default.
• W4386204408 cites W2035865653 @default.
• W4386204408 cites W2036477489 @default.
• W4386204408 cites W2044626437 @default.
• W4386204408 cites W2051593908 @default.
• W4386204408 cites W2054089600 @default.
• W4386204408 cites W2057072993 @default.
• W4386204408 cites W2057322782 @default.
• W4386204408 cites W2059864504 @default.
• W4386204408 cites W2066954128 @default.
• W4386204408 cites W2071447109 @default.
• W4386204408 cites W2078013557 @default.
• W4386204408 cites W2085870126 @default.
• W4386204408 cites W2086533330 @default.
• W4386204408 cites W2092867560 @default.
• W4386204408 cites W2094043869 @default.
• W4386204408 cites W2159030095 @default.
• W4386204408 cites W2537191486 @default.
• W4386204408 cites W2557557918 @default.
• W4386204408 cites W2561492449 @default.
• W4386204408 cites W2773634966 @default.
• W4386204408 cites W2789641625 @default.
• W4386204408 cites W2884296181 @default.
• W4386204408 cites W2886312433 @default.
• W4386204408 cites W2953134969 @default.
• W4386204408 cites W2972981935 @default.
• W4386204408 cites W2999929148 @default.
• W4386204408 cites W3087256598 @default.
• W4386204408 cites W3122056655 @default.
• W4386204408 cites W3168060753 @default.
• W4386204408 cites W3195928890 @default.
• W4386204408 cites W4220770746 @default.
• W4386204408 cites W4292092719 @default.
• W4386204408 cites W4306179274 @default.
• W4386204408 cites W4317756911 @default.
• W4386204408 cites W4319783093 @default.
• W4386204408 doi "https://doi.org/10.1016/j.actamat.2023.119291" @default.
• W4386204408 hasPublicationYear "2023" @default.
• W4386204408 type Work @default.
• W4386204408 citedByCount "0" @default.
• W4386204408 crossrefType "journal-article" @default.
• W4386204408 hasAuthorship W4386204408A5020823658 @default.
• W4386204408 hasAuthorship W4386204408A5074573081 @default.
• W4386204408 hasConcept C112950240 @default.
• W4386204408 hasConcept C159985019 @default.
• W4386204408 hasConcept C178790620 @default.
• W4386204408 hasConcept C184102282 @default.
• W4386204408 hasConcept C185592680 @default.
• W4386204408 hasConcept C18747287 @default.
• W4386204408 hasConcept C191897082 @default.
• W4386204408 hasConcept C192562407 @default.
• W4386204408 hasConcept C20625102 @default.
• W4386204408 hasConcept C2779930716 @default.
• W4386204408 hasConcept C43369102 @default.
• W4386204408 hasConcept C512968161 @default.
• W4386204408 hasConcept C87976508 @default.
• W4386204408 hasConcept C92621854 @default.
• W4386204408 hasConcept C96288455 @default.
• W4386204408 hasConceptScore W4386204408C112950240 @default.
• W4386204408 hasConceptScore W4386204408C159985019 @default.
• W4386204408 hasConceptScore W4386204408C178790620 @default.
• W4386204408 hasConceptScore W4386204408C184102282 @default.
• W4386204408 hasConceptScore W4386204408C185592680 @default.
• W4386204408 hasConceptScore W4386204408C18747287 @default.
• W4386204408 hasConceptScore W4386204408C191897082 @default.
• W4386204408 hasConceptScore W4386204408C192562407 @default.
• W4386204408 hasConceptScore W4386204408C20625102 @default.
• W4386204408 hasConceptScore W4386204408C2779930716 @default.
• W4386204408 hasConceptScore W4386204408C43369102 @default.
• W4386204408 hasConceptScore W4386204408C512968161 @default.
• W4386204408 hasConceptScore W4386204408C87976508 @default.
• W4386204408 hasConceptScore W4386204408C92621854 @default.
• W4386204408 hasConceptScore W4386204408C96288455 @default.
• W4386204408 hasLocation W43862044081 @default.
• W4386204408 hasOpenAccess W4386204408 @default.
• W4386204408 hasPrimaryLocation W43862044081 @default.
• W4386204408 hasRelatedWork W2029910392 @default.
• W4386204408 hasRelatedWork W2035525792 @default.
• W4386204408 hasRelatedWork W2087267419 @default.
• W4386204408 hasRelatedWork W2296547564 @default.
• W4386204408 hasRelatedWork W2888477419 @default.
• W4386204408 hasRelatedWork W2952859968 @default.
• W4386204408 hasRelatedWork W4309388012 @default.
• W4386204408 hasRelatedWork W4378390179 @default.

• next