• W4386258251 abstract "This article investigates the effect of nickel-induced finite plastic deformation at the friction interface of the CuSn10Bi3 bimetallic copper layer on its tribological properties. CuSn10Bi3 alloy bimetallic samples with different nickel contents were prepared by powder metallurgy, and the microstructure and Brinell hardness were observed. The tribological performances and wear behaviors under dry friction and oil-depleted lubrication conditions were evaluated and analyzed. The results show that the Ni in the copper-tin-based alloy reduces the surface porosity of the powder metallurgical samples. With the increase of Ni content from 0.5 wt.% to 1.2 wt.% and 2 wt.%, the porosity decreased by 36%, 48.7% and 62.3%, respectively, and the hardness of the samples increased slightly. The grain size of the alloy decreases with the increased Ni content, which is attributed to the increase of twinning. Besides, the friction coefficient of Ni-containing samples was more stable and the wear under dry friction was significantly reduced, especially, the wear loss is reduced by 78.2% when the content of Ni is 2%. The wear mechanism changed from abrasive-dominated and oxidative wear to plastic deformation-dominated and furrow wear. The limited plastic deformation of the friction interface caused by the addition of 2% nickel is a new strategy for solving the problem of brittle exfoliation of wear surfaces and improving the wear resistance of Bi-containing copper alloys." @default.
• W4386258251 created "2023-08-30" @default.
• W4386258251 creator A5000556982 @default.
• W4386258251 creator A5008795836 @default.
• W4386258251 creator A5021186573 @default.
• W4386258251 creator A5021570473 @default.
• W4386258251 creator A5034115721 @default.
• W4386258251 creator A5037269801 @default.
• W4386258251 creator A5061497257 @default.
• W4386258251 creator A5065419018 @default.
• W4386258251 creator A5065784891 @default.
• W4386258251 date "2023-10-01" @default.
• W4386258251 modified "2023-09-30" @default.
• W4386258251 title "The Effect of Nickel-Induced Finite Plasticity on the Tribological Behavior and Wear Resistance of Cu-Sn-Bi Alloy" @default.
• W4386258251 cites W1159008547 @default.
• W4386258251 cites W1436398272 @default.
• W4386258251 cites W1595109995 @default.
• W4386258251 cites W1965121867 @default.
• W4386258251 cites W1966055780 @default.
• W4386258251 cites W1989962260 @default.
• W4386258251 cites W2000096872 @default.
• W4386258251 cites W2024579383 @default.
• W4386258251 cites W2029927798 @default.
• W4386258251 cites W2043775985 @default.
• W4386258251 cites W2049577936 @default.
• W4386258251 cites W2051964150 @default.
• W4386258251 cites W2057919257 @default.
• W4386258251 cites W2077071506 @default.
• W4386258251 cites W2084499475 @default.
• W4386258251 cites W2085743724 @default.
• W4386258251 cites W2144844986 @default.
• W4386258251 cites W2404599864 @default.
• W4386258251 cites W2621205938 @default.
• W4386258251 cites W2755471007 @default.
• W4386258251 cites W2788319267 @default.
• W4386258251 cites W2906068156 @default.
• W4386258251 cites W3007516337 @default.
• W4386258251 cites W3017383805 @default.
• W4386258251 cites W3020978677 @default.
• W4386258251 cites W3021828225 @default.
• W4386258251 cites W3060312162 @default.
• W4386258251 cites W3096492206 @default.
• W4386258251 cites W3196966152 @default.
• W4386258251 cites W3201279744 @default.
• W4386258251 cites W3206889739 @default.
• W4386258251 cites W4281562932 @default.
• W4386258251 cites W4310195190 @default.
• W4386258251 cites W4362719759 @default.
• W4386258251 cites W4372218686 @default.
• W4386258251 doi "https://doi.org/10.1016/j.triboint.2023.108909" @default.
• W4386258251 hasPublicationYear "2023" @default.
• W4386258251 type Work @default.
• W4386258251 citedByCount "0" @default.
• W4386258251 crossrefType "journal-article" @default.
• W4386258251 hasAuthorship W4386258251A5000556982 @default.
• W4386258251 hasAuthorship W4386258251A5008795836 @default.
• W4386258251 hasAuthorship W4386258251A5021186573 @default.
• W4386258251 hasAuthorship W4386258251A5021570473 @default.
• W4386258251 hasAuthorship W4386258251A5034115721 @default.
• W4386258251 hasAuthorship W4386258251A5037269801 @default.
• W4386258251 hasAuthorship W4386258251A5061497257 @default.
• W4386258251 hasAuthorship W4386258251A5065419018 @default.
• W4386258251 hasAuthorship W4386258251A5065784891 @default.
• W4386258251 hasConcept C159985019 @default.
• W4386258251 hasConcept C167310744 @default.
• W4386258251 hasConcept C184608416 @default.
• W4386258251 hasConcept C191897082 @default.
• W4386258251 hasConcept C192191005 @default.
• W4386258251 hasConcept C192562407 @default.
• W4386258251 hasConcept C2780026712 @default.
• W4386258251 hasConcept C2780957350 @default.
• W4386258251 hasConcept C28369735 @default.
• W4386258251 hasConcept C504270822 @default.
• W4386258251 hasConcept C544778455 @default.
• W4386258251 hasConcept C6648577 @default.
• W4386258251 hasConcept C7794659 @default.
• W4386258251 hasConcept C87976508 @default.
• W4386258251 hasConceptScore W4386258251C159985019 @default.
• W4386258251 hasConceptScore W4386258251C167310744 @default.
• W4386258251 hasConceptScore W4386258251C184608416 @default.
• W4386258251 hasConceptScore W4386258251C191897082 @default.
• W4386258251 hasConceptScore W4386258251C192191005 @default.
• W4386258251 hasConceptScore W4386258251C192562407 @default.
• W4386258251 hasConceptScore W4386258251C2780026712 @default.
• W4386258251 hasConceptScore W4386258251C2780957350 @default.
• W4386258251 hasConceptScore W4386258251C28369735 @default.
• W4386258251 hasConceptScore W4386258251C504270822 @default.
• W4386258251 hasConceptScore W4386258251C544778455 @default.
• W4386258251 hasConceptScore W4386258251C6648577 @default.
• W4386258251 hasConceptScore W4386258251C7794659 @default.
• W4386258251 hasConceptScore W4386258251C87976508 @default.
• W4386258251 hasFunder F4320321001 @default.
• W4386258251 hasFunder F4320321133 @default.
• W4386258251 hasFunder F4320322880 @default.
• W4386258251 hasLocation W43862582511 @default.
• W4386258251 hasOpenAccess W4386258251 @default.
• W4386258251 hasPrimaryLocation W43862582511 @default.
• W4386258251 hasRelatedWork W2010733322 @default.

• next