- W4386435961 abstract "When the pressure leaching process of chalcopyrite is operated in the low and medium temperature range of 90℃~150℃, the sulfur component in chalcopyrite is converted to elemental sulfur, which suppresses the leaching of copper. In the present study, the copper leaching rate was improved by adding chloride ions and surfactants during the medium-temperature pressure leaching process at 150℃. Using the autoclave equipped with a 2L reactor made of titanium, a pressure leach tests were conducted for 180 min using 100g of chalcopyrite concentrate with D90 particle sizes of 10μm and 45μm in 5g/L and 50g/L sulfuric acid solutions. At 50g/L sulfuric acid solution without chloride ion and surfactant, when a sample with a D90 particle size of 45μm was used, the copper leaching efficiency after 180 min was 48%. As a result of leaching by adding 12g/L of chloride ions such as HCl, CuCl2, and NaCl, the leaching efficiencies increased to 96% and 97%, respectively, by adding HCl and CuCl2. As a result of a pressure leaching tests by adding surfactants of SLS (Sodium lignosulfonate) and CLS (calcium lignosulfonate), the leaching efficiency was over 99%. Consequentially, copper leaching efficiency increased when chloride ions and surfactants were added in 50g/L sulfuric acid solution." @default.
- W4386435961 created "2023-09-05" @default.
- W4386435961 creator A5009798125 @default.
- W4386435961 creator A5019852308 @default.
- W4386435961 creator A5027691876 @default.
- W4386435961 creator A5037631038 @default.
- W4386435961 creator A5079317230 @default.
- W4386435961 creator A5085642896 @default.
- W4386435961 date "2023-08-31" @default.
- W4386435961 modified "2023-10-01" @default.
- W4386435961 title "Effects of Chloride and Surfactant Addition on the Copper Leaching During Medium-temperature Pressure Leaching of Chalcopyrite" @default.
- W4386435961 cites W1966910451 @default.
- W4386435961 cites W2000097633 @default.
- W4386435961 cites W2045548339 @default.
- W4386435961 cites W2072588468 @default.
- W4386435961 cites W2078535735 @default.
- W4386435961 cites W2143788335 @default.
- W4386435961 cites W2149472400 @default.
- W4386435961 cites W2971346828 @default.
- W4386435961 cites W3211562476 @default.
- W4386435961 doi "https://doi.org/10.7844/kirr.2023.32.4.55" @default.
- W4386435961 hasPublicationYear "2023" @default.
- W4386435961 type Work @default.
- W4386435961 citedByCount "0" @default.
- W4386435961 crossrefType "journal-article" @default.
- W4386435961 hasAuthorship W4386435961A5009798125 @default.
- W4386435961 hasAuthorship W4386435961A5019852308 @default.
- W4386435961 hasAuthorship W4386435961A5027691876 @default.
- W4386435961 hasAuthorship W4386435961A5037631038 @default.
- W4386435961 hasAuthorship W4386435961A5079317230 @default.
- W4386435961 hasAuthorship W4386435961A5085642896 @default.
- W4386435961 hasBestOaLocation W43864359611 @default.
- W4386435961 hasConcept C109560049 @default.
- W4386435961 hasConcept C127313418 @default.
- W4386435961 hasConcept C13965031 @default.
- W4386435961 hasConcept C159390177 @default.
- W4386435961 hasConcept C159750122 @default.
- W4386435961 hasConcept C178790620 @default.
- W4386435961 hasConcept C179104552 @default.
- W4386435961 hasConcept C185592680 @default.
- W4386435961 hasConcept C2778188036 @default.
- W4386435961 hasConcept C2778199549 @default.
- W4386435961 hasConcept C2778695967 @default.
- W4386435961 hasConcept C518881349 @default.
- W4386435961 hasConcept C544778455 @default.
- W4386435961 hasConcept C90982505 @default.
- W4386435961 hasConceptScore W4386435961C109560049 @default.
- W4386435961 hasConceptScore W4386435961C127313418 @default.
- W4386435961 hasConceptScore W4386435961C13965031 @default.
- W4386435961 hasConceptScore W4386435961C159390177 @default.
- W4386435961 hasConceptScore W4386435961C159750122 @default.
- W4386435961 hasConceptScore W4386435961C178790620 @default.
- W4386435961 hasConceptScore W4386435961C179104552 @default.
- W4386435961 hasConceptScore W4386435961C185592680 @default.
- W4386435961 hasConceptScore W4386435961C2778188036 @default.
- W4386435961 hasConceptScore W4386435961C2778199549 @default.
- W4386435961 hasConceptScore W4386435961C2778695967 @default.
- W4386435961 hasConceptScore W4386435961C518881349 @default.
- W4386435961 hasConceptScore W4386435961C544778455 @default.
- W4386435961 hasConceptScore W4386435961C90982505 @default.
- W4386435961 hasIssue "4" @default.
- W4386435961 hasLocation W43864359611 @default.
- W4386435961 hasOpenAccess W4386435961 @default.
- W4386435961 hasPrimaryLocation W43864359611 @default.
- W4386435961 hasRelatedWork W1155296148 @default.
- W4386435961 hasRelatedWork W2084726267 @default.
- W4386435961 hasRelatedWork W2710243347 @default.
- W4386435961 hasRelatedWork W2792081274 @default.
- W4386435961 hasRelatedWork W2928094271 @default.
- W4386435961 hasRelatedWork W2980469276 @default.
- W4386435961 hasRelatedWork W3203736923 @default.
- W4386435961 hasRelatedWork W4206185782 @default.
- W4386435961 hasRelatedWork W4292566358 @default.
- W4386435961 hasRelatedWork W4383377443 @default.
- W4386435961 hasVolume "32" @default.
- W4386435961 isParatext "false" @default.
- W4386435961 isRetracted "false" @default.
- W4386435961 workType "article" @default.