- W4386484504 abstract "The microstructure, phase composition, hardness, and tensile properties of the Ti-48Al-2Cr-5Nb alloy have been systematically investigated using laser additive manufacturing technology. Results indicate that both the as-deposited and annealed microstructures contain both the α2 (Ti3Al) and γ (TiAl) phases. As the annealing temperature increased, the structure changed significantly from a large block structure to a fine equiaxed structure and finally to a large lamellar structure. Nevertheless, the amount and distribution of precipitation of α2 phase are obviously different, especially during the annealing at 1260 °C, where the fine α2 phases are evenly distributed on the γ phase matrix. The hardness value of the as-deposited sample is the highest, with a HV value of 484 at the room temperature, while the hardness value of the annealed sample at 1260 °C is the smallest, with a HV value of 344. An annealed sample at 1260 °C exhibits the highest tensile strength and elongation at room temperature, with values of 598 MPa and 2.1%, respectively. These values are increased by 1.15 times and 1.4 times compared to the as-deposited sample (519 MPa, 1.5%)." @default.
- W4386484504 created "2023-09-07" @default.
- W4386484504 creator A5016917580 @default.
- W4386484504 creator A5041268435 @default.
- W4386484504 creator A5061690729 @default.
- W4386484504 creator A5064542020 @default.
- W4386484504 creator A5084652695 @default.
- W4386484504 date "2023-09-06" @default.
- W4386484504 modified "2023-09-27" @default.
- W4386484504 title "Enhancement of Microstructure and Mechanical Properties of High Nb-TiAl Alloys Prepared Using Laser Additive Manufacturing by Annealing Treatment" @default.
- W4386484504 cites W1719252485 @default.
- W4386484504 cites W1792292627 @default.
- W4386484504 cites W1857469077 @default.
- W4386484504 cites W1977412026 @default.
- W4386484504 cites W1987360032 @default.
- W4386484504 cites W1990055138 @default.
- W4386484504 cites W1998057749 @default.
- W4386484504 cites W2007624231 @default.
- W4386484504 cites W2023055446 @default.
- W4386484504 cites W2033894157 @default.
- W4386484504 cites W2076051928 @default.
- W4386484504 cites W2076543518 @default.
- W4386484504 cites W2087879975 @default.
- W4386484504 cites W2520822460 @default.
- W4386484504 cites W2788898118 @default.
- W4386484504 cites W2793075517 @default.
- W4386484504 cites W2906465010 @default.
- W4386484504 cites W2909663813 @default.
- W4386484504 cites W2913470282 @default.
- W4386484504 cites W2920873927 @default.
- W4386484504 cites W2925080852 @default.
- W4386484504 cites W2951143914 @default.
- W4386484504 cites W2981514843 @default.
- W4386484504 cites W3016762086 @default.
- W4386484504 cites W3021789520 @default.
- W4386484504 cites W3093796124 @default.
- W4386484504 cites W3097032020 @default.
- W4386484504 cites W3165192201 @default.
- W4386484504 cites W3184328995 @default.
- W4386484504 cites W3187054411 @default.
- W4386484504 cites W4220710516 @default.
- W4386484504 cites W4283511476 @default.
- W4386484504 cites W4291298109 @default.
- W4386484504 cites W4304694002 @default.
- W4386484504 cites W4313252644 @default.
- W4386484504 cites W4313490854 @default.
- W4386484504 cites W4322505021 @default.
- W4386484504 cites W4322615302 @default.
- W4386484504 cites W4377229863 @default.
- W4386484504 doi "https://doi.org/10.3390/met13091562" @default.
- W4386484504 hasPublicationYear "2023" @default.
- W4386484504 type Work @default.
- W4386484504 citedByCount "0" @default.
- W4386484504 crossrefType "journal-article" @default.
- W4386484504 hasAuthorship W4386484504A5016917580 @default.
- W4386484504 hasAuthorship W4386484504A5041268435 @default.
- W4386484504 hasAuthorship W4386484504A5061690729 @default.
- W4386484504 hasAuthorship W4386484504A5064542020 @default.
- W4386484504 hasAuthorship W4386484504A5084652695 @default.
- W4386484504 hasBestOaLocation W43864845041 @default.
- W4386484504 hasConcept C112950240 @default.
- W4386484504 hasConcept C159985019 @default.
- W4386484504 hasConcept C191897082 @default.
- W4386484504 hasConcept C192562407 @default.
- W4386484504 hasConcept C2777855556 @default.
- W4386484504 hasConcept C2780026712 @default.
- W4386484504 hasConcept C33947775 @default.
- W4386484504 hasConcept C77851909 @default.
- W4386484504 hasConcept C81710450 @default.
- W4386484504 hasConcept C87976508 @default.
- W4386484504 hasConceptScore W4386484504C112950240 @default.
- W4386484504 hasConceptScore W4386484504C159985019 @default.
- W4386484504 hasConceptScore W4386484504C191897082 @default.
- W4386484504 hasConceptScore W4386484504C192562407 @default.
- W4386484504 hasConceptScore W4386484504C2777855556 @default.
- W4386484504 hasConceptScore W4386484504C2780026712 @default.
- W4386484504 hasConceptScore W4386484504C33947775 @default.
- W4386484504 hasConceptScore W4386484504C77851909 @default.
- W4386484504 hasConceptScore W4386484504C81710450 @default.
- W4386484504 hasConceptScore W4386484504C87976508 @default.
- W4386484504 hasIssue "9" @default.
- W4386484504 hasLocation W43864845041 @default.
- W4386484504 hasOpenAccess W4386484504 @default.
- W4386484504 hasPrimaryLocation W43864845041 @default.
- W4386484504 hasRelatedWork W1979107336 @default.
- W4386484504 hasRelatedWork W2043583991 @default.
- W4386484504 hasRelatedWork W2348697288 @default.
- W4386484504 hasRelatedWork W2357499900 @default.
- W4386484504 hasRelatedWork W2365897911 @default.
- W4386484504 hasRelatedWork W2369154548 @default.
- W4386484504 hasRelatedWork W2371235204 @default.
- W4386484504 hasRelatedWork W2377322010 @default.
- W4386484504 hasRelatedWork W2379439189 @default.
- W4386484504 hasRelatedWork W4240267549 @default.
- W4386484504 hasVolume "13" @default.
- W4386484504 isParatext "false" @default.
- W4386484504 isRetracted "false" @default.
- W4386484504 workType "article" @default.