• W4386894559 abstract "With the development of laser surface modification techniques like direct laser metal deposition (DLMD), titanium alloy (TI6Al4V) may now have its entire base metal microstructure preserved while having its surface modified to have better characteristics. Numerous surface issues in the aerospace industry can be resolved using this method without changing the titanium alloy’s primary microstructure. As a result, titanium alloy is now more widely used in sectors outside of aerospace and automotive. This is made possible by fabricating metal composite coatings on titanium alloys using the same DLMD method. Any component can be repaired using this method, thereby extending the component’s life. The experimental process was carried out utilizing a 3000 W Ytterbium Laser System at the National Laser Centre of the CSIR in South Africa. Through the use of a laser system, AlCuTi/Ti6Al4V was created. The characterization of the materials for grinding and polishing was performed according to standard methods. There is a substantial correlation between the reinforcement feed rate, scan speed, and laser power components. Due to the significant role that aluminum reinforcement played and the presence of aluminum in the base metal structure, Ti-Al structures were also created. The reaction and solidification of the copper and aluminum reinforcements in the melt pool produced the dendritic phases visible in the microstructures. Compared to the base alloy, the microhardness’s highest value of 1117.2 HV1.0 is equivalent to a 69.1% enhancement in the hardness of the composite coatings. The enhanced hardness property is linked to the dendritic phases formed in the microstructures as a result of optimized process parameters. Tensile strengths of laser-clad ternary coatings also improved by 23%, 46.2%, 13.1%, 70%, 34.3%, and 51.7% when compared to titanium alloy substrates. The yield strengths of laser-clad ternary coatings improved by 19%, 46.7%, 12.9%, 69.3%, 34.7%, and 52.1% when compared to the titanium alloy substrate." @default.
• W4386894559 created "2023-09-21" @default.
• W4386894559 creator A5027048459 @default.
• W4386894559 creator A5091238139 @default.
• W4386894559 date "2023-09-19" @default.
• W4386894559 modified "2023-09-27" @default.
• W4386894559 title "The Interplay of Thermal Gradient and Laser Process Parameters on the Mechanical Properties, Geometrical and Microstructural Characteristics of Laser-Cladded Titanium (Ti6Al4V) Alloy Composite Coatings" @default.
• W4386894559 cites W164058520 @default.
• W4386894559 cites W1990812423 @default.
• W4386894559 cites W1998109070 @default.
• W4386894559 cites W2037962563 @default.
• W4386894559 cites W2038107483 @default.
• W4386894559 cites W2075082207 @default.
• W4386894559 cites W2110610796 @default.
• W4386894559 cites W2336082409 @default.
• W4386894559 cites W2519118040 @default.
• W4386894559 cites W2590341273 @default.
• W4386894559 cites W2754192061 @default.
• W4386894559 cites W2762367303 @default.
• W4386894559 cites W2790447540 @default.
• W4386894559 cites W2798305321 @default.
• W4386894559 cites W2798770586 @default.
• W4386894559 cites W2803003386 @default.
• W4386894559 cites W2808336794 @default.
• W4386894559 cites W2900215463 @default.
• W4386894559 cites W2905634162 @default.
• W4386894559 cites W2909923143 @default.
• W4386894559 cites W2947401340 @default.
• W4386894559 cites W2970719415 @default.
• W4386894559 cites W2980496446 @default.
• W4386894559 cites W2989959927 @default.
• W4386894559 cites W2994245114 @default.
• W4386894559 cites W2997098239 @default.
• W4386894559 cites W2999493289 @default.
• W4386894559 cites W3002558971 @default.
• W4386894559 cites W3007220773 @default.
• W4386894559 cites W3008648887 @default.
• W4386894559 cites W3019680958 @default.
• W4386894559 cites W3043478361 @default.
• W4386894559 cites W3048294379 @default.
• W4386894559 cites W3110920230 @default.
• W4386894559 cites W3122934104 @default.
• W4386894559 cites W3136331239 @default.
• W4386894559 cites W3209609010 @default.
• W4386894559 cites W4281775406 @default.
• W4386894559 cites W4290777144 @default.
• W4386894559 cites W4291944857 @default.
• W4386894559 cites W4294578750 @default.
• W4386894559 cites W4315641767 @default.
• W4386894559 cites W4366285987 @default.
• W4386894559 cites W4386380123 @default.
• W4386894559 doi "https://doi.org/10.3390/met13091617" @default.
• W4386894559 hasPublicationYear "2023" @default.
• W4386894559 type Work @default.
• W4386894559 citedByCount "0" @default.
• W4386894559 crossrefType "journal-article" @default.
• W4386894559 hasAuthorship W4386894559A5027048459 @default.
• W4386894559 hasAuthorship W4386894559A5091238139 @default.
• W4386894559 hasBestOaLocation W43868945591 @default.
• W4386894559 hasConcept C104779481 @default.
• W4386894559 hasConcept C120665830 @default.
• W4386894559 hasConcept C121332964 @default.
• W4386894559 hasConcept C159985019 @default.
• W4386894559 hasConcept C165720898 @default.
• W4386894559 hasConcept C191897082 @default.
• W4386894559 hasConcept C192562407 @default.
• W4386894559 hasConcept C200649887 @default.
• W4386894559 hasConcept C2780026712 @default.
• W4386894559 hasConcept C506065880 @default.
• W4386894559 hasConcept C520434653 @default.
• W4386894559 hasConcept C87976508 @default.
• W4386894559 hasConcept C8953137 @default.
• W4386894559 hasConceptScore W4386894559C104779481 @default.
• W4386894559 hasConceptScore W4386894559C120665830 @default.
• W4386894559 hasConceptScore W4386894559C121332964 @default.
• W4386894559 hasConceptScore W4386894559C159985019 @default.
• W4386894559 hasConceptScore W4386894559C165720898 @default.
• W4386894559 hasConceptScore W4386894559C191897082 @default.
• W4386894559 hasConceptScore W4386894559C192562407 @default.
• W4386894559 hasConceptScore W4386894559C200649887 @default.
• W4386894559 hasConceptScore W4386894559C2780026712 @default.
• W4386894559 hasConceptScore W4386894559C506065880 @default.
• W4386894559 hasConceptScore W4386894559C520434653 @default.
• W4386894559 hasConceptScore W4386894559C87976508 @default.
• W4386894559 hasConceptScore W4386894559C8953137 @default.
• W4386894559 hasIssue "9" @default.
• W4386894559 hasLocation W43868945591 @default.
• W4386894559 hasOpenAccess W4386894559 @default.
• W4386894559 hasPrimaryLocation W43868945591 @default.
• W4386894559 hasRelatedWork W2010582503 @default.
• W4386894559 hasRelatedWork W2010733322 @default.
• W4386894559 hasRelatedWork W2068113961 @default.
• W4386894559 hasRelatedWork W2123155170 @default.
• W4386894559 hasRelatedWork W2301725003 @default.
• W4386894559 hasRelatedWork W2379855728 @default.
• W4386894559 hasRelatedWork W3118359290 @default.
• W4386894559 hasRelatedWork W3167402195 @default.
• W4386894559 hasRelatedWork W4205648827 @default.

• next