- W4386929949 abstract "Deposition of (Ti-Al)N/MoN multilayered coatings was carried out through a cathodic ion-plating system in an argon and then nitrogen atmosphere. Bilayer thickness (Λ) of all the samples were achieved, from 22 to 104 nm, by organizing substrate holder rotational speed (SRS). To obtain the optimum properties of the (Ti-Al)N/MoN coatings, the Ti and Al ratio was maintained at a level of 1:1. X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS), and Raman spectroscopy were utilized to analyze the crystal structure and morphology of the coatings. Mechanical and tribological properties were examined by nanohardness and atomic force microscopy (AFM). The preferred orientation of the (Ti-Al)N/MoN nanoscale multilayer films was TiAlN (200) and MoN (200), which had face centered cubic (fcc) and hexagonal structures, respectively. The hardness increased with the decrease in Λ (104 nm to 26 nm), and then it increased. The highest hardness of 37 GPa was revealed at Λ = 26 nm, whereas the least wear rate of 8.09 × 10−7 mm3/N.m was attained at Λ = 22 nm. Wear rate, roughness, and coefficient of friction were decreased with decreasing bilayer period. EDS results showed that Al and Ti contents were almost the same in all samples, as per design of the experiment." @default.
- W4386929949 created "2023-09-22" @default.
- W4386929949 creator A5005981909 @default.
- W4386929949 creator A5013444155 @default.
- W4386929949 creator A5013642381 @default.
- W4386929949 creator A5057452324 @default.
- W4386929949 creator A5086387667 @default.
- W4386929949 date "2023-09-21" @default.
- W4386929949 modified "2023-09-29" @default.
- W4386929949 title "Influence of Bilayer Thickness on Mechanical and Tribological Properties of (Ti-Al)N/MoN Nanostructured Hard Coatings Deposited by Cathodic Arc Ion Plating" @default.
- W4386929949 cites W1971513670 @default.
- W4386929949 cites W1971936954 @default.
- W4386929949 cites W1972393222 @default.
- W4386929949 cites W1974809930 @default.
- W4386929949 cites W1976560842 @default.
- W4386929949 cites W1979753997 @default.
- W4386929949 cites W1983099270 @default.
- W4386929949 cites W1990537103 @default.
- W4386929949 cites W1991897258 @default.
- W4386929949 cites W1994889016 @default.
- W4386929949 cites W1997898669 @default.
- W4386929949 cites W1998420404 @default.
- W4386929949 cites W2002751337 @default.
- W4386929949 cites W2003841352 @default.
- W4386929949 cites W2003942779 @default.
- W4386929949 cites W2009172438 @default.
- W4386929949 cites W2011086867 @default.
- W4386929949 cites W2012356267 @default.
- W4386929949 cites W2013925377 @default.
- W4386929949 cites W2023053552 @default.
- W4386929949 cites W2035599240 @default.
- W4386929949 cites W2046010281 @default.
- W4386929949 cites W2046301931 @default.
- W4386929949 cites W2047188972 @default.
- W4386929949 cites W2051688097 @default.
- W4386929949 cites W2053966030 @default.
- W4386929949 cites W2054331114 @default.
- W4386929949 cites W2057404088 @default.
- W4386929949 cites W2058330774 @default.
- W4386929949 cites W2059394375 @default.
- W4386929949 cites W2062197393 @default.
- W4386929949 cites W2066691087 @default.
- W4386929949 cites W2067147848 @default.
- W4386929949 cites W2067881756 @default.
- W4386929949 cites W2071320900 @default.
- W4386929949 cites W2072088376 @default.
- W4386929949 cites W2072242654 @default.
- W4386929949 cites W2074619246 @default.
- W4386929949 cites W2079475325 @default.
- W4386929949 cites W2079533933 @default.
- W4386929949 cites W2079567509 @default.
- W4386929949 cites W2079944220 @default.
- W4386929949 cites W2081010317 @default.
- W4386929949 cites W2086514778 @default.
- W4386929949 cites W2089487204 @default.
- W4386929949 cites W2089722667 @default.
- W4386929949 cites W2093181131 @default.
- W4386929949 cites W2107898214 @default.
- W4386929949 cites W2108478370 @default.
- W4386929949 cites W2131590988 @default.
- W4386929949 cites W2142059122 @default.
- W4386929949 cites W2145182511 @default.
- W4386929949 cites W2147934360 @default.
- W4386929949 cites W2293584318 @default.
- W4386929949 cites W2473773761 @default.
- W4386929949 doi "https://doi.org/10.3390/coatings13091654" @default.
- W4386929949 hasPublicationYear "2023" @default.
- W4386929949 type Work @default.
- W4386929949 citedByCount "0" @default.
- W4386929949 crossrefType "journal-article" @default.
- W4386929949 hasAuthorship W4386929949A5005981909 @default.
- W4386929949 hasAuthorship W4386929949A5013444155 @default.
- W4386929949 hasAuthorship W4386929949A5013642381 @default.
- W4386929949 hasAuthorship W4386929949A5057452324 @default.
- W4386929949 hasAuthorship W4386929949A5086387667 @default.
- W4386929949 hasBestOaLocation W43869299491 @default.
- W4386929949 hasConcept C111368507 @default.
- W4386929949 hasConcept C113196181 @default.
- W4386929949 hasConcept C118442862 @default.
- W4386929949 hasConcept C120665830 @default.
- W4386929949 hasConcept C121332964 @default.
- W4386929949 hasConcept C127313418 @default.
- W4386929949 hasConcept C127413603 @default.
- W4386929949 hasConcept C146088050 @default.
- W4386929949 hasConcept C159985019 @default.
- W4386929949 hasConcept C161368742 @default.
- W4386929949 hasConcept C167310744 @default.
- W4386929949 hasConcept C171250308 @default.
- W4386929949 hasConcept C175708663 @default.
- W4386929949 hasConcept C185592680 @default.
- W4386929949 hasConcept C19067145 @default.
- W4386929949 hasConcept C191897082 @default.
- W4386929949 hasConcept C192157962 @default.
- W4386929949 hasConcept C192562407 @default.
- W4386929949 hasConcept C26771246 @default.
- W4386929949 hasConcept C2777289219 @default.
- W4386929949 hasConcept C40003534 @default.
- W4386929949 hasConcept C41625074 @default.