- W4387009969 abstract "In this work, the effects of brine quenching on the mechanical properties and microstructural attributes of AISI 304 steel have been analysed. For a reference purpose, one sample was kept in ‘as-received’ condition. Three steel plates were treated at 800oC for 1 hour, 1.5 hour and 2 hours respectively. The heated samples were cooled inside brine solution up to room temperature. For mechanical property analysis, all the four plates were cut into standard sized specimens for tensile test, hardness test and toughness test. The microstructural analysis reveals that pitting corrosion has affected the γ-grains as well as δ-boundaries. The ‘as-received’ samples have shown the highest value of ultimate tensile strength (UTS) i.e., 940 MPa with 59.5% of elongation whereas the third heat treated sample, which was heated for 2 hours, has shown a decrement of 13% and 55% in UTS and elongation respectively as compared to these of ‘as received’ sample. As a result of Cr-deterioration and carbide dissolution at grain boundaries, an increase in hardness was recorded in the heat-treated samples. Also, the lowest toughness, 35% lower than as received sample, was recorded in the third sample which are heated for a long period." @default.
- W4387009969 created "2023-09-26" @default.
- W4387009969 creator A5004129947 @default.
- W4387009969 creator A5092934083 @default.
- W4387009969 date "2023-09-25" @default.
- W4387009969 modified "2023-09-26" @default.
- W4387009969 title "ANALYSING THE EFFECT OF THERMAL TREATMENT WITH AN AID OF BRINE QUENCHING ON MICROSTRUCTURAL CHARACTERISTICS AND PHYSICAL PROPERTIES OF AISI-304 PLATES" @default.
- W4387009969 doi "https://doi.org/10.36547/ams.29.3.1826" @default.
- W4387009969 hasPublicationYear "2023" @default.
- W4387009969 type Work @default.
- W4387009969 citedByCount "0" @default.
- W4387009969 crossrefType "journal-article" @default.
- W4387009969 hasAuthorship W4387009969A5004129947 @default.
- W4387009969 hasAuthorship W4387009969A5092934083 @default.
- W4387009969 hasBestOaLocation W43870099691 @default.
- W4387009969 hasConcept C112950240 @default.
- W4387009969 hasConcept C121332964 @default.
- W4387009969 hasConcept C121745418 @default.
- W4387009969 hasConcept C159985019 @default.
- W4387009969 hasConcept C182508753 @default.
- W4387009969 hasConcept C191897082 @default.
- W4387009969 hasConcept C192562407 @default.
- W4387009969 hasConcept C2776957854 @default.
- W4387009969 hasConcept C33947775 @default.
- W4387009969 hasConcept C47908070 @default.
- W4387009969 hasConcept C5335593 @default.
- W4387009969 hasConcept C62520636 @default.
- W4387009969 hasConcept C87976508 @default.
- W4387009969 hasConcept C91881484 @default.
- W4387009969 hasConcept C97355855 @default.
- W4387009969 hasConcept C99595764 @default.
- W4387009969 hasConceptScore W4387009969C112950240 @default.
- W4387009969 hasConceptScore W4387009969C121332964 @default.
- W4387009969 hasConceptScore W4387009969C121745418 @default.
- W4387009969 hasConceptScore W4387009969C159985019 @default.
- W4387009969 hasConceptScore W4387009969C182508753 @default.
- W4387009969 hasConceptScore W4387009969C191897082 @default.
- W4387009969 hasConceptScore W4387009969C192562407 @default.
- W4387009969 hasConceptScore W4387009969C2776957854 @default.
- W4387009969 hasConceptScore W4387009969C33947775 @default.
- W4387009969 hasConceptScore W4387009969C47908070 @default.
- W4387009969 hasConceptScore W4387009969C5335593 @default.
- W4387009969 hasConceptScore W4387009969C62520636 @default.
- W4387009969 hasConceptScore W4387009969C87976508 @default.
- W4387009969 hasConceptScore W4387009969C91881484 @default.
- W4387009969 hasConceptScore W4387009969C97355855 @default.
- W4387009969 hasConceptScore W4387009969C99595764 @default.
- W4387009969 hasIssue "3" @default.
- W4387009969 hasLocation W43870099691 @default.
- W4387009969 hasOpenAccess W4387009969 @default.
- W4387009969 hasPrimaryLocation W43870099691 @default.
- W4387009969 hasRelatedWork W1986314249 @default.
- W4387009969 hasRelatedWork W1995944114 @default.
- W4387009969 hasRelatedWork W2077723265 @default.
- W4387009969 hasRelatedWork W2375443292 @default.
- W4387009969 hasRelatedWork W2394138227 @default.
- W4387009969 hasRelatedWork W3007171949 @default.
- W4387009969 hasRelatedWork W3133955656 @default.
- W4387009969 hasRelatedWork W3155537323 @default.
- W4387009969 hasRelatedWork W4240267549 @default.
- W4387009969 hasRelatedWork W855883057 @default.
- W4387009969 hasVolume "29" @default.
- W4387009969 isParatext "false" @default.
- W4387009969 isRetracted "false" @default.
- W4387009969 workType "article" @default.