- W4387244204 abstract "Oily sludge (OS), a hazardous waste that generated in the process of petroleum exploration, utilized as raw material in this study for preparation of high value-added glass-ceramics. The effect of CaF2 addition and temperature on the melting behavior, crystallization mechanism, physical-chemical properties and heavy metals leaching of glass-ceramics was highlighted. The results indicated that the obtained parent glass demonstrated completely amorphous structure at 1200 °C when CaF2 content was 4 wt.%. The addition of CaF2 improved crystallinity of glass-ceramics, which further improved the glass-ceramics properties. Comparing the properties of OC-1200-830 with OCF4-1030, it was observed that the density increased from 2.27 g/cm3 to 2.60 g/cm3, compressive strength increased from 56.43 MPa to 122.00 MPa, bending strength increased from 6.16 MPa to 11.41 MPa, acid resistance increased from 92.8% to 96.8%, alkali resistance increased from 94.6% to 98.2%, and water absorption reduced from 0.19% to 0.12%. The leaching concentrations of heavy metals in the glass-ceramics were below than the thresholds required in GB 5058.3–2007, China. The theoretical energy consumption of glass-ceramics melted at 1200 °C was 30.84%–41.37% lower than that melted at 1500 °C, which demonstrated that the glass-ceramics prepared in this study have cost advantages." @default.
- W4387244204 created "2023-10-03" @default.
- W4387244204 creator A5001877853 @default.
- W4387244204 creator A5005280344 @default.
- W4387244204 creator A5008141480 @default.
- W4387244204 creator A5010718874 @default.
- W4387244204 creator A5059431543 @default.
- W4387244204 creator A5071833362 @default.
- W4387244204 date "2023-10-01" @default.
- W4387244204 modified "2023-10-03" @default.
- W4387244204 title "Preparation of oily sludge-derived glass-ceramics by low-temperature melting with addition of CaF2" @default.
- W4387244204 cites W1971812616 @default.
- W4387244204 cites W1990433513 @default.
- W4387244204 cites W1992006144 @default.
- W4387244204 cites W1993917774 @default.
- W4387244204 cites W2013878283 @default.
- W4387244204 cites W2019760442 @default.
- W4387244204 cites W2020239977 @default.
- W4387244204 cites W2030736249 @default.
- W4387244204 cites W2032146192 @default.
- W4387244204 cites W2049506136 @default.
- W4387244204 cites W2060904958 @default.
- W4387244204 cites W2066000540 @default.
- W4387244204 cites W2082121747 @default.
- W4387244204 cites W2088173077 @default.
- W4387244204 cites W2094976959 @default.
- W4387244204 cites W2135948296 @default.
- W4387244204 cites W2303837560 @default.
- W4387244204 cites W2531837203 @default.
- W4387244204 cites W2773966967 @default.
- W4387244204 cites W2885145943 @default.
- W4387244204 cites W2918359229 @default.
- W4387244204 cites W2939512285 @default.
- W4387244204 cites W2947567660 @default.
- W4387244204 cites W2953828811 @default.
- W4387244204 cites W2962824775 @default.
- W4387244204 cites W2986979634 @default.
- W4387244204 cites W3001994075 @default.
- W4387244204 cites W3002768088 @default.
- W4387244204 cites W3014833487 @default.
- W4387244204 cites W3015338248 @default.
- W4387244204 cites W3021422425 @default.
- W4387244204 cites W3027044479 @default.
- W4387244204 cites W3039143085 @default.
- W4387244204 cites W3042521111 @default.
- W4387244204 cites W3046343777 @default.
- W4387244204 cites W3164564061 @default.
- W4387244204 cites W3182153401 @default.
- W4387244204 cites W3192608198 @default.
- W4387244204 cites W3214995459 @default.
- W4387244204 cites W4200301589 @default.
- W4387244204 cites W4223900598 @default.
- W4387244204 cites W4292381899 @default.
- W4387244204 cites W4304189324 @default.
- W4387244204 cites W4316259221 @default.
- W4387244204 cites W4318346446 @default.
- W4387244204 doi "https://doi.org/10.1016/j.ceramint.2023.10.004" @default.
- W4387244204 hasPublicationYear "2023" @default.
- W4387244204 type Work @default.
- W4387244204 citedByCount "0" @default.
- W4387244204 crossrefType "journal-article" @default.
- W4387244204 hasAuthorship W4387244204A5001877853 @default.
- W4387244204 hasAuthorship W4387244204A5005280344 @default.
- W4387244204 hasAuthorship W4387244204A5008141480 @default.
- W4387244204 hasAuthorship W4387244204A5010718874 @default.
- W4387244204 hasAuthorship W4387244204A5059431543 @default.
- W4387244204 hasAuthorship W4387244204A5071833362 @default.
- W4387244204 hasConcept C121332964 @default.
- W4387244204 hasConcept C127413603 @default.
- W4387244204 hasConcept C134132462 @default.
- W4387244204 hasConcept C159390177 @default.
- W4387244204 hasConcept C159750122 @default.
- W4387244204 hasConcept C159985019 @default.
- W4387244204 hasConcept C178790620 @default.
- W4387244204 hasConcept C185592680 @default.
- W4387244204 hasConcept C185903656 @default.
- W4387244204 hasConcept C191897082 @default.
- W4387244204 hasConcept C192562407 @default.
- W4387244204 hasConcept C198091228 @default.
- W4387244204 hasConcept C199289684 @default.
- W4387244204 hasConcept C203036418 @default.
- W4387244204 hasConcept C206139338 @default.
- W4387244204 hasConcept C2776276667 @default.
- W4387244204 hasConcept C30407753 @default.
- W4387244204 hasConcept C39432304 @default.
- W4387244204 hasConcept C42360764 @default.
- W4387244204 hasConcept C46275449 @default.
- W4387244204 hasConcept C56052488 @default.
- W4387244204 hasConcept C62520636 @default.
- W4387244204 hasConcept C90982505 @default.
- W4387244204 hasConceptScore W4387244204C121332964 @default.
- W4387244204 hasConceptScore W4387244204C127413603 @default.
- W4387244204 hasConceptScore W4387244204C134132462 @default.
- W4387244204 hasConceptScore W4387244204C159390177 @default.
- W4387244204 hasConceptScore W4387244204C159750122 @default.
- W4387244204 hasConceptScore W4387244204C159985019 @default.
- W4387244204 hasConceptScore W4387244204C178790620 @default.
- W4387244204 hasConceptScore W4387244204C185592680 @default.
- W4387244204 hasConceptScore W4387244204C185903656 @default.
- W4387244204 hasConceptScore W4387244204C191897082 @default.