- W4387609957 abstract "Abstract Cemented carbide 91 wt% WC–3 wt% TiC–6 wt% Co was sintered by spark plasma sintering at different temperatures of 1200 °C, 1300 °C, and 1400 °C and the effect of sintering temperature on the microstructure and properties of this type of composites, such as total density, apparent density, hardness, and fracture surface were measured and observed using Field Emission-Scanning Electron Microscopy, Optical Microscopy, X-ray diffractometry and mechanical test instruments. The results showed that the apparent density of the samples increased with increasing sintering temperature from 1200 to 1300 °C from 13.98 to 14.23 g/cm 3 , respectively. But in the sample sintered at 1400 °C, the density was reduced to 14.20 g/cm 3 . An increase in the fluidity of the cobalt phase and capillary pressure is the cause of the increase in density at higher temperatures, the cobalt phase has evaporated and the density has decreased slightly. Also, Vickers micro-hardness results showed that the hardness of sintered samples increased with the increase of sintering temperature. For the sample sintered at 1200 °C the hardness value of 1746.41 kgf/mm 2 was obtained which increased with increasing sintering temperature from 1300 to 1400 °C from 2094.33 to 2280.97 kgf/mm 2 , respectively. The amount of core–shell structure [including TiC-core and (W, Ti)C-shell] increased with increasing the sintering temperature process. As a result, the hardness also increased. At the optimum sintering temperature, it was found that TiC inhibited the grain growth of tungsten carbide. In addition, as expected, the grain growth of tungsten carbide increased with increasing sintering temperatures. Examination of the fracture surface of sintered samples at different temperatures also showed that brittle fracture involves fracture." @default.
- W4387609957 created "2023-10-14" @default.
- W4387609957 creator A5017407160 @default.
- W4387609957 creator A5047207876 @default.
- W4387609957 creator A5052220085 @default.
- W4387609957 creator A5083931732 @default.
- W4387609957 date "2023-10-13" @default.
- W4387609957 modified "2023-10-14" @default.
- W4387609957 title "Microstructure and mechanical properties of WC–TiC–Co cemented carbides produced by spark plasma sintering (SPS) method" @default.
- W4387609957 cites W1222277907 @default.
- W4387609957 cites W1461665492 @default.
- W4387609957 cites W1976079357 @default.
- W4387609957 cites W1978014090 @default.
- W4387609957 cites W1988844564 @default.
- W4387609957 cites W1993082775 @default.
- W4387609957 cites W1999145304 @default.
- W4387609957 cites W2005874629 @default.
- W4387609957 cites W2006082205 @default.
- W4387609957 cites W2022006213 @default.
- W4387609957 cites W2036075944 @default.
- W4387609957 cites W2041621348 @default.
- W4387609957 cites W2047845550 @default.
- W4387609957 cites W2052929949 @default.
- W4387609957 cites W2070384333 @default.
- W4387609957 cites W2076352852 @default.
- W4387609957 cites W2077158160 @default.
- W4387609957 cites W2092756133 @default.
- W4387609957 cites W2092956937 @default.
- W4387609957 cites W2093884617 @default.
- W4387609957 cites W2094198893 @default.
- W4387609957 cites W2106495332 @default.
- W4387609957 cites W2120442825 @default.
- W4387609957 cites W2124520421 @default.
- W4387609957 cites W2268216698 @default.
- W4387609957 cites W2313408525 @default.
- W4387609957 cites W2412230573 @default.
- W4387609957 cites W2464430323 @default.
- W4387609957 cites W2516417027 @default.
- W4387609957 cites W2553646193 @default.
- W4387609957 cites W2558216459 @default.
- W4387609957 cites W2581018726 @default.
- W4387609957 cites W2793429686 @default.
- W4387609957 cites W2884070826 @default.
- W4387609957 cites W2905432151 @default.
- W4387609957 cites W3160729612 @default.
- W4387609957 cites W3216939938 @default.
- W4387609957 cites W4210796826 @default.
- W4387609957 cites W776657707 @default.
- W4387609957 cites W990022193 @default.
- W4387609957 doi "https://doi.org/10.1007/s42452-023-05510-9" @default.
- W4387609957 hasPublicationYear "2023" @default.
- W4387609957 type Work @default.
- W4387609957 citedByCount "0" @default.
- W4387609957 crossrefType "journal-article" @default.
- W4387609957 hasAuthorship W4387609957A5017407160 @default.
- W4387609957 hasAuthorship W4387609957A5047207876 @default.
- W4387609957 hasAuthorship W4387609957A5052220085 @default.
- W4387609957 hasAuthorship W4387609957A5083931732 @default.
- W4387609957 hasBestOaLocation W43876099571 @default.
- W4387609957 hasConcept C133392424 @default.
- W4387609957 hasConcept C159985019 @default.
- W4387609957 hasConcept C178405089 @default.
- W4387609957 hasConcept C191897082 @default.
- W4387609957 hasConcept C192562407 @default.
- W4387609957 hasConcept C26771246 @default.
- W4387609957 hasConcept C2776014600 @default.
- W4387609957 hasConcept C2777581544 @default.
- W4387609957 hasConcept C5335593 @default.
- W4387609957 hasConcept C82455628 @default.
- W4387609957 hasConcept C87976508 @default.
- W4387609957 hasConcept C98390173 @default.
- W4387609957 hasConceptScore W4387609957C133392424 @default.
- W4387609957 hasConceptScore W4387609957C159985019 @default.
- W4387609957 hasConceptScore W4387609957C178405089 @default.
- W4387609957 hasConceptScore W4387609957C191897082 @default.
- W4387609957 hasConceptScore W4387609957C192562407 @default.
- W4387609957 hasConceptScore W4387609957C26771246 @default.
- W4387609957 hasConceptScore W4387609957C2776014600 @default.
- W4387609957 hasConceptScore W4387609957C2777581544 @default.
- W4387609957 hasConceptScore W4387609957C5335593 @default.
- W4387609957 hasConceptScore W4387609957C82455628 @default.
- W4387609957 hasConceptScore W4387609957C87976508 @default.
- W4387609957 hasConceptScore W4387609957C98390173 @default.
- W4387609957 hasIssue "11" @default.
- W4387609957 hasLocation W43876099571 @default.
- W4387609957 hasOpenAccess W4387609957 @default.
- W4387609957 hasPrimaryLocation W43876099571 @default.
- W4387609957 hasRelatedWork W1010533511 @default.
- W4387609957 hasRelatedWork W1501633259 @default.
- W4387609957 hasRelatedWork W1965024206 @default.
- W4387609957 hasRelatedWork W1994903329 @default.
- W4387609957 hasRelatedWork W2009453507 @default.
- W4387609957 hasRelatedWork W2335131106 @default.
- W4387609957 hasRelatedWork W2385903672 @default.
- W4387609957 hasRelatedWork W2743509240 @default.
- W4387609957 hasRelatedWork W3000691972 @default.
- W4387609957 hasRelatedWork W3025728734 @default.
- W4387609957 hasVolume "5" @default.
- W4387609957 isParatext "false" @default.
- W4387609957 isRetracted "false" @default.