- W4387614035 abstract "Weight plays a significant role in the automotive and aerospace fields due to the demand of lightweight material structures. A lighter body in weight (BIW) and in structure can reduce fuel consumption, lessen emissions, and support the SDGs 9, 11, 12, and 13. Therefore, polyurethane (PU) foam is suitable for applications that require low weight. The characteristics of hybrid polyurethane-graphite micro were successfully evaluated in this study. Several tests have been used to characterize these structures, such as, compression, hardness, density, surface evaluation, and FTIR analysis. The results showed that the expansion and shrinkage variations lead to different shapes at specific ratios. Compression tests show that the highest value occurred at 0.84 kN, with a 4:1 ratio found in pure PU foam without any reinforcement. PU foam with 2% graphite filler showed the highest results at the 4:1 ratio with a value of 0.45 kN. Furthermore, the highest hardness test result was 37.7 SHD. Density testing indicates that the highest value is obtained from specimens with a 4:1 ratio of 0.077 g/cm3. FTIR testing reveals that adding graphite as a filler alters the chemical bonds during the formation of solid PU foam. Surface observations show that adding graphite as a filler influences the variation in material structure formation. All the evaluation has tended to conclude the present combination as suitable for lightweight structures applications." @default.
- W4387614035 created "2023-10-14" @default.
- W4387614035 creator A5001752079 @default.
- W4387614035 creator A5002865644 @default.
- W4387614035 creator A5004042219 @default.
- W4387614035 creator A5023787907 @default.
- W4387614035 creator A5030318103 @default.
- W4387614035 creator A5032140853 @default.
- W4387614035 creator A5034888838 @default.
- W4387614035 creator A5044029581 @default.
- W4387614035 creator A5073653459 @default.
- W4387614035 date "2023-10-13" @default.
- W4387614035 modified "2023-10-15" @default.
- W4387614035 title "Excellent Hybrid Polyurethane-Graphite Filler Micro Powder As a Lightweight Structure" @default.
- W4387614035 cites W1658188934 @default.
- W4387614035 cites W1965996296 @default.
- W4387614035 cites W1987729589 @default.
- W4387614035 cites W1999946995 @default.
- W4387614035 cites W2001259318 @default.
- W4387614035 cites W2008366372 @default.
- W4387614035 cites W2009140435 @default.
- W4387614035 cites W2019244294 @default.
- W4387614035 cites W2057611100 @default.
- W4387614035 cites W2082728408 @default.
- W4387614035 cites W2084260394 @default.
- W4387614035 cites W2090602676 @default.
- W4387614035 cites W2209180023 @default.
- W4387614035 cites W2482647437 @default.
- W4387614035 cites W2555680828 @default.
- W4387614035 cites W2587473795 @default.
- W4387614035 cites W2606912664 @default.
- W4387614035 cites W2615774883 @default.
- W4387614035 cites W2751309852 @default.
- W4387614035 cites W2799522486 @default.
- W4387614035 cites W2921345164 @default.
- W4387614035 cites W2923052517 @default.
- W4387614035 cites W2943935493 @default.
- W4387614035 cites W2969788844 @default.
- W4387614035 cites W2970965941 @default.
- W4387614035 cites W3015715638 @default.
- W4387614035 cites W3034793486 @default.
- W4387614035 cites W3036259373 @default.
- W4387614035 cites W3037806170 @default.
- W4387614035 cites W3112651073 @default.
- W4387614035 cites W3130286226 @default.
- W4387614035 cites W3130983841 @default.
- W4387614035 cites W3134137598 @default.
- W4387614035 cites W3199745216 @default.
- W4387614035 cites W3213518765 @default.
- W4387614035 cites W4224105684 @default.
- W4387614035 cites W4224320551 @default.
- W4387614035 cites W4247845842 @default.
- W4387614035 cites W4281646744 @default.
- W4387614035 cites W4285403818 @default.
- W4387614035 cites W4303628998 @default.
- W4387614035 cites W4310154017 @default.
- W4387614035 cites W4313557225 @default.
- W4387614035 cites W4313575583 @default.
- W4387614035 cites W4353048060 @default.
- W4387614035 cites W4379115245 @default.
- W4387614035 cites W4381094900 @default.
- W4387614035 doi "https://doi.org/10.3390/jcs7100433" @default.
- W4387614035 hasPublicationYear "2023" @default.
- W4387614035 type Work @default.
- W4387614035 citedByCount "0" @default.
- W4387614035 crossrefType "journal-article" @default.
- W4387614035 hasAuthorship W4387614035A5001752079 @default.
- W4387614035 hasAuthorship W4387614035A5002865644 @default.
- W4387614035 hasAuthorship W4387614035A5004042219 @default.
- W4387614035 hasAuthorship W4387614035A5023787907 @default.
- W4387614035 hasAuthorship W4387614035A5030318103 @default.
- W4387614035 hasAuthorship W4387614035A5032140853 @default.
- W4387614035 hasAuthorship W4387614035A5034888838 @default.
- W4387614035 hasAuthorship W4387614035A5044029581 @default.
- W4387614035 hasAuthorship W4387614035A5073653459 @default.
- W4387614035 hasBestOaLocation W43876140351 @default.
- W4387614035 hasConcept C127413603 @default.
- W4387614035 hasConcept C159985019 @default.
- W4387614035 hasConcept C160892712 @default.
- W4387614035 hasConcept C180145272 @default.
- W4387614035 hasConcept C192562407 @default.
- W4387614035 hasConcept C2778223994 @default.
- W4387614035 hasConcept C2779578285 @default.
- W4387614035 hasConcept C2779698641 @default.
- W4387614035 hasConcept C42360764 @default.
- W4387614035 hasConceptScore W4387614035C127413603 @default.
- W4387614035 hasConceptScore W4387614035C159985019 @default.
- W4387614035 hasConceptScore W4387614035C160892712 @default.
- W4387614035 hasConceptScore W4387614035C180145272 @default.
- W4387614035 hasConceptScore W4387614035C192562407 @default.
- W4387614035 hasConceptScore W4387614035C2778223994 @default.
- W4387614035 hasConceptScore W4387614035C2779578285 @default.
- W4387614035 hasConceptScore W4387614035C2779698641 @default.
- W4387614035 hasConceptScore W4387614035C42360764 @default.
- W4387614035 hasIssue "10" @default.
- W4387614035 hasLocation W43876140351 @default.
- W4387614035 hasOpenAccess W4387614035 @default.
- W4387614035 hasPrimaryLocation W43876140351 @default.