- W4387643911 abstract "In this work, oxide-free AlN coating was fabricated using single-step, large throughput nitrogen-shrouded plasma spraying. Initially, Al/AlN composite feedstock powder was prepared by a ball-milling at a 70:30 wt.% ratio to deposit the AlN coating. Microstructural evaluation revealed the formation of dominant c-AlN phase along with minor h-AlN without presence of any oxides or impurities in the coating. Hardness and elastic modulus (E) were observed to be ~7.2 GPa and ~280 GPa respectively. Furthermore, an investigation of tribological performance showed the wear rate ~0.18 × 10-3 mm3/Nm and coefficient of friction (COF) 0.45 ± 0.02. In addition, the corrosion resistance behaviour of AlN coating in 3.5 wt.% NaCl shows as low as 2.95×10-9 mm/s indicates the extended life of the coated components. Therefore, the fabricated plasma-sprayed AlN coating can be recommended for high-performing wear and anti-corrosive competitor for industrial applications." @default.
- W4387643911 created "2023-10-15" @default.
- W4387643911 creator A5023366727 @default.
- W4387643911 creator A5039144771 @default.
- W4387643911 creator A5044908817 @default.
- W4387643911 creator A5060566951 @default.
- W4387643911 creator A5067452929 @default.
- W4387643911 creator A5069307992 @default.
- W4387643911 creator A5080182527 @default.
- W4387643911 creator A5093064618 @default.
- W4387643911 date "2023-10-01" @default.
- W4387643911 modified "2023-10-15" @default.
- W4387643911 title "Plasma sprayed aluminium nitride (AlN) coating: Microstructural, Mechanical, Tribological, and Corrosion resistance performance" @default.
- W4387643911 cites W1447850574 @default.
- W4387643911 cites W1964109089 @default.
- W4387643911 cites W1975460003 @default.
- W4387643911 cites W1979319857 @default.
- W4387643911 cites W1982026068 @default.
- W4387643911 cites W2026015040 @default.
- W4387643911 cites W2047481790 @default.
- W4387643911 cites W2054142788 @default.
- W4387643911 cites W2070207023 @default.
- W4387643911 cites W2080478413 @default.
- W4387643911 cites W2081052176 @default.
- W4387643911 cites W2083611773 @default.
- W4387643911 cites W2101950335 @default.
- W4387643911 cites W2103185019 @default.
- W4387643911 cites W2127931975 @default.
- W4387643911 cites W2148669051 @default.
- W4387643911 cites W2153589086 @default.
- W4387643911 cites W2158164257 @default.
- W4387643911 cites W2560680979 @default.
- W4387643911 cites W2900641840 @default.
- W4387643911 cites W2904077491 @default.
- W4387643911 cites W2920813842 @default.
- W4387643911 cites W2946516151 @default.
- W4387643911 cites W2981602838 @default.
- W4387643911 cites W3131847665 @default.
- W4387643911 cites W3155674520 @default.
- W4387643911 cites W3158632467 @default.
- W4387643911 cites W4210921601 @default.
- W4387643911 cites W4281911016 @default.
- W4387643911 cites W4285603421 @default.
- W4387643911 doi "https://doi.org/10.1016/j.jeurceramsoc.2023.10.027" @default.
- W4387643911 hasPublicationYear "2023" @default.
- W4387643911 type Work @default.
- W4387643911 citedByCount "0" @default.
- W4387643911 crossrefType "journal-article" @default.
- W4387643911 hasAuthorship W4387643911A5023366727 @default.
- W4387643911 hasAuthorship W4387643911A5039144771 @default.
- W4387643911 hasAuthorship W4387643911A5044908817 @default.
- W4387643911 hasAuthorship W4387643911A5060566951 @default.
- W4387643911 hasAuthorship W4387643911A5067452929 @default.
- W4387643911 hasAuthorship W4387643911A5069307992 @default.
- W4387643911 hasAuthorship W4387643911A5080182527 @default.
- W4387643911 hasAuthorship W4387643911A5093064618 @default.
- W4387643911 hasConcept C159985019 @default.
- W4387643911 hasConcept C167310744 @default.
- W4387643911 hasConcept C191897082 @default.
- W4387643911 hasConcept C192562407 @default.
- W4387643911 hasConcept C194760766 @default.
- W4387643911 hasConcept C20625102 @default.
- W4387643911 hasConcept C2779227376 @default.
- W4387643911 hasConcept C2780243435 @default.
- W4387643911 hasConcept C2781448156 @default.
- W4387643911 hasConcept C513153333 @default.
- W4387643911 hasConceptScore W4387643911C159985019 @default.
- W4387643911 hasConceptScore W4387643911C167310744 @default.
- W4387643911 hasConceptScore W4387643911C191897082 @default.
- W4387643911 hasConceptScore W4387643911C192562407 @default.
- W4387643911 hasConceptScore W4387643911C194760766 @default.
- W4387643911 hasConceptScore W4387643911C20625102 @default.
- W4387643911 hasConceptScore W4387643911C2779227376 @default.
- W4387643911 hasConceptScore W4387643911C2780243435 @default.
- W4387643911 hasConceptScore W4387643911C2781448156 @default.
- W4387643911 hasConceptScore W4387643911C513153333 @default.
- W4387643911 hasFunder F4320321024 @default.
- W4387643911 hasLocation W43876439111 @default.
- W4387643911 hasOpenAccess W4387643911 @default.
- W4387643911 hasPrimaryLocation W43876439111 @default.
- W4387643911 hasRelatedWork W1510657699 @default.
- W4387643911 hasRelatedWork W2024908392 @default.
- W4387643911 hasRelatedWork W2039721274 @default.
- W4387643911 hasRelatedWork W2062635693 @default.
- W4387643911 hasRelatedWork W2091129523 @default.
- W4387643911 hasRelatedWork W2576374239 @default.
- W4387643911 hasRelatedWork W2766764309 @default.
- W4387643911 hasRelatedWork W3205459232 @default.
- W4387643911 hasRelatedWork W657245677 @default.
- W4387643911 hasRelatedWork W2469895656 @default.
- W4387643911 isParatext "false" @default.
- W4387643911 isRetracted "false" @default.
- W4387643911 workType "article" @default.