- W4387668822 abstract "This paper describes the microstructure evolution and phase transformation of residue from the lateritic nickel ore high-pressure acid leaching (HPAL) during carbothermic reduction using palm kernel shell (PKS) charcoal as a reductant. The study consisted of thermodynamic calculations combined with analysis of reduction experiments. The thermodynamic assessment predicted that the main phases formed during the reduction process were γ-Fe metal, liquid metal, slag, and spinel, with abundance of reducing gas (CO and H2) at the temperature range of 750–1500 °C. The experimental study shows that the resulting product upon cooling was sponge iron or direct reduced iron when HPAL residue-PKS charcoal composites were reacted up to 1400 °C for 45 min. The sponge iron had an average apparent density of 5.8 ± 0.1 g/cm3 and a 90.8 ± 0.4% metallization degree. The microstructure analysis revealed that as the reduction time was increased, small iron nuggets began forming on the surface of the reduced product. By addition of Na2CO3, the separation of iron nuggets from slag appeared to be improved, hence enhancing the overall reduction process. Furthermore, iron nuggets’ highest apparent density and metallization degree were obtained at 7 ± 0.1 g/cm3 and 98 ± 0.5%, respectively, when adding Na2CO3 of 6 wt %. The phase and microstructure analyses also revealed that the iron nuggets comprised coarse pearlite, eutectic cementite, ledeburite, and sulfides. Thus, this study offers alternative sustainable process conditions for simultaneously handling the HPAL residue using PKS waste to produce metallic iron." @default.
- W4387668822 created "2023-10-17" @default.
- W4387668822 creator A5012799600 @default.
- W4387668822 creator A5033187845 @default.
- W4387668822 creator A5058208484 @default.
- W4387668822 creator A5079936496 @default.
- W4387668822 creator A5081478348 @default.
- W4387668822 date "2023-10-16" @default.
- W4387668822 modified "2023-10-17" @default.
- W4387668822 title "Microstructure Evolution and Phase Transformation of Iron Produced from the Sustainable Carbothermic Reduction Process of High-Pressure Acid Leaching Residue" @default.
- W4387668822 cites W1567690746 @default.
- W4387668822 cites W1980455397 @default.
- W4387668822 cites W1996463317 @default.
- W4387668822 cites W2002629165 @default.
- W4387668822 cites W2007945283 @default.
- W4387668822 cites W2021112989 @default.
- W4387668822 cites W2059994155 @default.
- W4387668822 cites W2071620750 @default.
- W4387668822 cites W2073034603 @default.
- W4387668822 cites W2086188363 @default.
- W4387668822 cites W2179450873 @default.
- W4387668822 cites W2254323733 @default.
- W4387668822 cites W2621159585 @default.
- W4387668822 cites W2626326648 @default.
- W4387668822 cites W2742854983 @default.
- W4387668822 cites W2748260403 @default.
- W4387668822 cites W3003994067 @default.
- W4387668822 cites W3006994995 @default.
- W4387668822 cites W3047551616 @default.
- W4387668822 cites W3176196993 @default.
- W4387668822 cites W3211674443 @default.
- W4387668822 cites W4205247519 @default.
- W4387668822 cites W4206648991 @default.
- W4387668822 cites W4252619099 @default.
- W4387668822 cites W4281478309 @default.
- W4387668822 cites W4281824975 @default.
- W4387668822 cites W4283364343 @default.
- W4387668822 cites W4320484042 @default.
- W4387668822 cites W4321769999 @default.
- W4387668822 cites W4322109848 @default.
- W4387668822 doi "https://doi.org/10.1021/acsomega.3c05574" @default.
- W4387668822 hasPublicationYear "2023" @default.
- W4387668822 type Work @default.
- W4387668822 citedByCount "0" @default.
- W4387668822 crossrefType "journal-article" @default.
- W4387668822 hasAuthorship W4387668822A5012799600 @default.
- W4387668822 hasAuthorship W4387668822A5033187845 @default.
- W4387668822 hasAuthorship W4387668822A5058208484 @default.
- W4387668822 hasAuthorship W4387668822A5079936496 @default.
- W4387668822 hasAuthorship W4387668822A5081478348 @default.
- W4387668822 hasBestOaLocation W43876688221 @default.
- W4387668822 hasConcept C159390177 @default.
- W4387668822 hasConcept C159750122 @default.
- W4387668822 hasConcept C18168003 @default.
- W4387668822 hasConcept C191897082 @default.
- W4387668822 hasConcept C192562407 @default.
- W4387668822 hasConcept C2776230739 @default.
- W4387668822 hasConcept C2781297133 @default.
- W4387668822 hasConcept C39432304 @default.
- W4387668822 hasConcept C544153396 @default.
- W4387668822 hasConcept C5701217 @default.
- W4387668822 hasConcept C87976508 @default.
- W4387668822 hasConcept C90982505 @default.
- W4387668822 hasConcept C96288455 @default.
- W4387668822 hasConceptScore W4387668822C159390177 @default.
- W4387668822 hasConceptScore W4387668822C159750122 @default.
- W4387668822 hasConceptScore W4387668822C18168003 @default.
- W4387668822 hasConceptScore W4387668822C191897082 @default.
- W4387668822 hasConceptScore W4387668822C192562407 @default.
- W4387668822 hasConceptScore W4387668822C2776230739 @default.
- W4387668822 hasConceptScore W4387668822C2781297133 @default.
- W4387668822 hasConceptScore W4387668822C39432304 @default.
- W4387668822 hasConceptScore W4387668822C544153396 @default.
- W4387668822 hasConceptScore W4387668822C5701217 @default.
- W4387668822 hasConceptScore W4387668822C87976508 @default.
- W4387668822 hasConceptScore W4387668822C90982505 @default.
- W4387668822 hasConceptScore W4387668822C96288455 @default.
- W4387668822 hasFunder F4320319804 @default.
- W4387668822 hasFunder F4320337167 @default.
- W4387668822 hasLocation W43876688221 @default.
- W4387668822 hasOpenAccess W4387668822 @default.
- W4387668822 hasPrimaryLocation W43876688221 @default.
- W4387668822 hasRelatedWork W189897711 @default.
- W4387668822 hasRelatedWork W2073161244 @default.
- W4387668822 hasRelatedWork W2094866033 @default.
- W4387668822 hasRelatedWork W2307942246 @default.
- W4387668822 hasRelatedWork W2322753709 @default.
- W4387668822 hasRelatedWork W2385985812 @default.
- W4387668822 hasRelatedWork W2761271274 @default.
- W4387668822 hasRelatedWork W2950189844 @default.
- W4387668822 hasRelatedWork W3023709432 @default.
- W4387668822 hasRelatedWork W3173460233 @default.
- W4387668822 isParatext "false" @default.
- W4387668822 isRetracted "false" @default.
- W4387668822 workType "article" @default.