- W48689972 abstract "Extruded profiles of AlMgSi-alloys are widely used in various industries such as the automotive industry, aerospace and in the oil and gas industry. To tailor the alloys for specific needs and applications, more information about the behaviour of alloying elements is needed. In this study, extruded profiles of AA6082 have been examined. Seven different alloys with increasing content of Mn have been subjected to three homogenisation procedures. The purpose of the different homogenisation procedures was to obtain different densities of dispersoids, while still maintaining the same level of elements in solid solution. The study have examined the effect of Mn and homogenisation procedure on grain structure, strength and corrosion behaviour. Results from this study showed that the density of dispersoids greatly affect the final grain structure after extrusion. Homogenisation variants that contained a high density of dispersoids showed low degree of recrystallisation. Increasing amount of Mn also contributed to a lower degree of recrystallisation. In as extruded condition variants with a high density of dipersoids were harder than variants with lower density, despite equal chemistry and elements in solid solution. At peak strength, increased content of Mn led to a reduction in strength." @default.
- W48689972 created "2016-06-24" @default.
- W48689972 creator A5033025135 @default.
- W48689972 date "2014-01-01" @default.
- W48689972 modified "2023-09-24" @default.
- W48689972 title "The Effect of Mn and Homogenisation Procedure on Mechanical Properties and Grain Structure in Extruded AA6082" @default.
- W48689972 hasPublicationYear "2014" @default.
- W48689972 type Work @default.
- W48689972 sameAs 48689972 @default.
- W48689972 citedByCount "0" @default.
- W48689972 crossrefType "dissertation" @default.
- W48689972 hasAuthorship W48689972A5033025135 @default.
- W48689972 hasConcept C191897082 @default.
- W48689972 hasConcept C192191005 @default.
- W48689972 hasConcept C192562407 @default.
- W48689972 hasConcept C2778958987 @default.
- W48689972 hasConcept C87976508 @default.
- W48689972 hasConceptScore W48689972C191897082 @default.
- W48689972 hasConceptScore W48689972C192191005 @default.
- W48689972 hasConceptScore W48689972C192562407 @default.
- W48689972 hasConceptScore W48689972C2778958987 @default.
- W48689972 hasConceptScore W48689972C87976508 @default.
- W48689972 hasLocation W486899721 @default.
- W48689972 hasOpenAccess W48689972 @default.
- W48689972 hasPrimaryLocation W486899721 @default.
- W48689972 hasRelatedWork W113780691 @default.
- W48689972 hasRelatedWork W1508320396 @default.
- W48689972 hasRelatedWork W1596660070 @default.
- W48689972 hasRelatedWork W1852574487 @default.
- W48689972 hasRelatedWork W1991043393 @default.
- W48689972 hasRelatedWork W2018687177 @default.
- W48689972 hasRelatedWork W2040275478 @default.
- W48689972 hasRelatedWork W2076774968 @default.
- W48689972 hasRelatedWork W2081638232 @default.
- W48689972 hasRelatedWork W2128015464 @default.
- W48689972 hasRelatedWork W2243327768 @default.
- W48689972 hasRelatedWork W2299455136 @default.
- W48689972 hasRelatedWork W2514555691 @default.
- W48689972 hasRelatedWork W3003697565 @default.
- W48689972 hasRelatedWork W3023383902 @default.
- W48689972 hasRelatedWork W3135756698 @default.
- W48689972 hasRelatedWork W313746750 @default.
- W48689972 hasRelatedWork W577419624 @default.
- W48689972 hasRelatedWork W806189902 @default.
- W48689972 hasRelatedWork W94199809 @default.
- W48689972 isParatext "false" @default.
- W48689972 isRetracted "false" @default.
- W48689972 magId "48689972" @default.
- W48689972 workType "dissertation" @default.