- W48857087 abstract "Effect of indigenous cement on high temperature slag corrosion resistance of four different types of industrial ULCC composition has been investigated. Four type were as follows: (a)composition dominated by BFA aggregate, (b) composition dominated by WFA aggregate,(b) composition dominated by Densed Bauxite aggregate and (b) composition having Densed Bauxite fused alumina aggregate. Two types of CA plus CA2 based indigenous cements; (i) 70% Al2O3 containing and (ii) 80% Al2O3 containing, were investigated for the study. One established imported cement was also used to compare the properties of ULCC based on Indigenous cement. ULCC precast were prepared by industrial procedure such as; mixing of aggregates, cement and additives, granulometry, addition of water and casting, curing at room temperature and drying at 110oC. Physical, mechanical and thermo mechanical properties of ULCC were evaluated on as dried, 1000oC and 1450oC fired samples. Slag corrosion resistivity was tested in rotary drum by using 50:50 slag and metal.It has been found that ULCC composition having higher amount of BFA aggregate shows better slag corrosion resistance when indigenous HAC are used. However ULCC containing WFA shows better slag resistance when 80% Al2O3 containing indigenous cement were used. It was found that slag resistivity mainly depend on fused alumina aggregate content of ULCC and compositions without having BFA and WFA shows very high (about 28%) erosion. It has been found that Fused Alumina aggregates are less prone slag erosion than Densed Bauxite. But with addition of WFA, the Slag erosion resistivity of Densed Bauxite based ULCC increases.70% Al2O3 containing indigenous cement shows better erosion resistivity performance in presence of BFA. However 80%Al2O3 containing indigenous cement shows better performance in presence of WFA." @default.
- W48857087 created "2016-06-24" @default.
- W48857087 creator A5081798500 @default.
- W48857087 date "2009-06-20" @default.
- W48857087 modified "2023-09-26" @default.
- W48857087 title "Study of Erosion Resistance of ULCC based Precast with Indigenous High Alumina Cement" @default.
- W48857087 cites W1980698579 @default.
- W48857087 cites W1994432438 @default.
- W48857087 cites W2040191376 @default.
- W48857087 cites W2046142926 @default.
- W48857087 cites W2061594311 @default.
- W48857087 cites W2068474514 @default.
- W48857087 cites W2078039643 @default.
- W48857087 cites W2083469233 @default.
- W48857087 cites W2084104250 @default.
- W48857087 cites W2086500166 @default.
- W48857087 cites W2089465676 @default.
- W48857087 cites W2095042540 @default.
- W48857087 cites W2097316063 @default.
- W48857087 cites W2102405774 @default.
- W48857087 cites W2111563188 @default.
- W48857087 cites W2553439263 @default.
- W48857087 cites W956712873 @default.
- W48857087 hasPublicationYear "2009" @default.
- W48857087 type Work @default.
- W48857087 sameAs 48857087 @default.
- W48857087 citedByCount "2" @default.
- W48857087 countsByYear W488570872013 @default.
- W48857087 countsByYear W488570872014 @default.
- W48857087 crossrefType "dissertation" @default.
- W48857087 hasAuthorship W48857087A5081798500 @default.
- W48857087 hasConcept C132976073 @default.
- W48857087 hasConcept C159048435 @default.
- W48857087 hasConcept C159985019 @default.
- W48857087 hasConcept C191897082 @default.
- W48857087 hasConcept C192562407 @default.
- W48857087 hasConcept C20625102 @default.
- W48857087 hasConcept C2778163720 @default.
- W48857087 hasConcept C4679612 @default.
- W48857087 hasConcept C523993062 @default.
- W48857087 hasConcept C87343466 @default.
- W48857087 hasConceptScore W48857087C132976073 @default.
- W48857087 hasConceptScore W48857087C159048435 @default.
- W48857087 hasConceptScore W48857087C159985019 @default.
- W48857087 hasConceptScore W48857087C191897082 @default.
- W48857087 hasConceptScore W48857087C192562407 @default.
- W48857087 hasConceptScore W48857087C20625102 @default.
- W48857087 hasConceptScore W48857087C2778163720 @default.
- W48857087 hasConceptScore W48857087C4679612 @default.
- W48857087 hasConceptScore W48857087C523993062 @default.
- W48857087 hasConceptScore W48857087C87343466 @default.
- W48857087 hasLocation W488570871 @default.
- W48857087 hasOpenAccess W48857087 @default.
- W48857087 hasPrimaryLocation W488570871 @default.
- W48857087 hasRelatedWork W1497688861 @default.
- W48857087 hasRelatedWork W1567863699 @default.
- W48857087 hasRelatedWork W1967560567 @default.
- W48857087 hasRelatedWork W1984747042 @default.
- W48857087 hasRelatedWork W2054400615 @default.
- W48857087 hasRelatedWork W2068205672 @default.
- W48857087 hasRelatedWork W2072127453 @default.
- W48857087 hasRelatedWork W2141134037 @default.
- W48857087 hasRelatedWork W221531866 @default.
- W48857087 hasRelatedWork W2361971028 @default.
- W48857087 hasRelatedWork W2362879328 @default.
- W48857087 hasRelatedWork W2388969890 @default.
- W48857087 hasRelatedWork W2391869513 @default.
- W48857087 hasRelatedWork W2469913553 @default.
- W48857087 hasRelatedWork W2980124036 @default.
- W48857087 hasRelatedWork W643711465 @default.
- W48857087 hasRelatedWork W790619821 @default.
- W48857087 hasRelatedWork W2500957280 @default.
- W48857087 hasRelatedWork W2842004949 @default.
- W48857087 hasRelatedWork W3122170383 @default.
- W48857087 isParatext "false" @default.
- W48857087 isRetracted "false" @default.
- W48857087 magId "48857087" @default.
- W48857087 workType "dissertation" @default.