- W58776605 endingPage "334" @default.
- W58776605 startingPage "327" @default.
- W58776605 abstract "Residual stress of the Fe-Zn coating layer on GA (galvannealed) steel was analyzed by means of the finite element analysis. The experimentally observed result that the coating layer has been fractured in the as supplied samples was accounted for by the analyzed high tensile residual stress introduced in the Fe-Zn coating layer due to the difference in coefficient of thermal expansion between the coating layer and the substrate steel during cooling from the galvannealing temperature. The multiple fracture phenomenon of the coating layer under the thermally induced residual stress was explained as the stress-relaxation process. From the stress analysis for the measured average crack spacing in the coating layer on the IF (Interstitial Free) and SPCC (Steel Plate Cold Commercial) steel substrates, the tensile strength of the coating layer was estimated to be 260-270 MPa. Concerning the influence of the coating layer thickness on the multiple cracking, it was revealed that the crack spacing increases with increasing thickness of the coating layer and it is proportional to the thickness of the coating layer if the strength of the coating layer is insensitive to length and thickness. Concerning the influence of the stress-strain behavior of the substrate on the multiple cracking, it was shown that the multiple cracking progresses more when the substrate steel has higher yield- and plastic flowstress." @default.
- W58776605 created "2016-06-24" @default.
- W58776605 creator A5028874166 @default.
- W58776605 creator A5034921693 @default.
- W58776605 creator A5041965608 @default.
- W58776605 creator A5044065525 @default.
- W58776605 creator A5052812642 @default.
- W58776605 creator A5056465893 @default.
- W58776605 creator A5083376423 @default.
- W58776605 date "2005-01-01" @default.
- W58776605 modified "2023-10-05" @default.
- W58776605 title "Residual Stress Analysis and Estimation of Strength of Fe-Zn Coating Layer of Galvannealed Steel by Means of Finite Element Method" @default.
- W58776605 cites W1965494467 @default.
- W58776605 cites W1978442820 @default.
- W58776605 cites W1983122814 @default.
- W58776605 cites W1986026470 @default.
- W58776605 cites W2000707929 @default.
- W58776605 cites W2004799181 @default.
- W58776605 cites W2011779942 @default.
- W58776605 cites W2012590851 @default.
- W58776605 cites W2035005132 @default.
- W58776605 cites W2044371446 @default.
- W58776605 cites W2075131623 @default.
- W58776605 cites W2076249607 @default.
- W58776605 cites W2093671237 @default.
- W58776605 cites W2727420541 @default.
- W58776605 doi "https://doi.org/10.2355/tetsutohagane1955.91.3_327" @default.
- W58776605 hasPublicationYear "2005" @default.
- W58776605 type Work @default.
- W58776605 sameAs 58776605 @default.
- W58776605 citedByCount "3" @default.
- W58776605 crossrefType "journal-article" @default.
- W58776605 hasAuthorship W58776605A5028874166 @default.
- W58776605 hasAuthorship W58776605A5034921693 @default.
- W58776605 hasAuthorship W58776605A5041965608 @default.
- W58776605 hasAuthorship W58776605A5044065525 @default.
- W58776605 hasAuthorship W58776605A5052812642 @default.
- W58776605 hasAuthorship W58776605A5056465893 @default.
- W58776605 hasAuthorship W58776605A5083376423 @default.
- W58776605 hasBestOaLocation W587766051 @default.
- W58776605 hasConcept C111368507 @default.
- W58776605 hasConcept C112950240 @default.
- W58776605 hasConcept C127313418 @default.
- W58776605 hasConcept C138885662 @default.
- W58776605 hasConcept C159985019 @default.
- W58776605 hasConcept C191897082 @default.
- W58776605 hasConcept C192562407 @default.
- W58776605 hasConcept C21036866 @default.
- W58776605 hasConcept C22144681 @default.
- W58776605 hasConcept C2777289219 @default.
- W58776605 hasConcept C2779227376 @default.
- W58776605 hasConcept C2781448156 @default.
- W58776605 hasConcept C37292000 @default.
- W58776605 hasConcept C41895202 @default.
- W58776605 hasConcept C58396970 @default.
- W58776605 hasConcept C8846229 @default.
- W58776605 hasConceptScore W58776605C111368507 @default.
- W58776605 hasConceptScore W58776605C112950240 @default.
- W58776605 hasConceptScore W58776605C127313418 @default.
- W58776605 hasConceptScore W58776605C138885662 @default.
- W58776605 hasConceptScore W58776605C159985019 @default.
- W58776605 hasConceptScore W58776605C191897082 @default.
- W58776605 hasConceptScore W58776605C192562407 @default.
- W58776605 hasConceptScore W58776605C21036866 @default.
- W58776605 hasConceptScore W58776605C22144681 @default.
- W58776605 hasConceptScore W58776605C2777289219 @default.
- W58776605 hasConceptScore W58776605C2779227376 @default.
- W58776605 hasConceptScore W58776605C2781448156 @default.
- W58776605 hasConceptScore W58776605C37292000 @default.
- W58776605 hasConceptScore W58776605C41895202 @default.
- W58776605 hasConceptScore W58776605C58396970 @default.
- W58776605 hasConceptScore W58776605C8846229 @default.
- W58776605 hasIssue "3" @default.
- W58776605 hasLocation W587766051 @default.
- W58776605 hasOpenAccess W58776605 @default.
- W58776605 hasPrimaryLocation W587766051 @default.
- W58776605 hasRelatedWork W1981720211 @default.
- W58776605 hasRelatedWork W2029673849 @default.
- W58776605 hasRelatedWork W2049943583 @default.
- W58776605 hasRelatedWork W2089085266 @default.
- W58776605 hasRelatedWork W2094854567 @default.
- W58776605 hasRelatedWork W2319313457 @default.
- W58776605 hasRelatedWork W2369831604 @default.
- W58776605 hasRelatedWork W2729932191 @default.
- W58776605 hasRelatedWork W2795554382 @default.
- W58776605 hasRelatedWork W2921624399 @default.
- W58776605 hasVolume "91" @default.
- W58776605 isParatext "false" @default.
- W58776605 isRetracted "false" @default.
- W58776605 magId "58776605" @default.
- W58776605 workType "article" @default.