- W599677788 abstract "To study the bake-hardening behavior of Cu added Al-1%Mg2Si alloys by the tensile test after resistivity measurement, resistivity of many samples taken from a rolled sheet was measured in various stages of heat treatment. The resistivity ρSTQ in the 848 K-3.6 ks solution treated and water quenched state (STQ) fluctuated within ranges of 0.9 to 1.7 nΩm. There were good linear relations between the ρSTQ and resistivity after room temperature pre-aging for 1 day (ρRTP) for each of four alloys. The ρRTP values were maintained after short period final aging at 448 K. Possible causes of the fluctuation in ρ were checked. Effects of the STQ conditions on the ρSTQ were negligible. Because the Matthiessen plot of the ρRTP gave good straight lines having acceptable gradient, the fluctuation is not due to errors in size factor and resistance. Change in room temperature showed no correlation with increment up to the ρRTP. Therefore, it is concluded that the ρSTQ of rolled plates used in a series of study have a stripe shaped distribution of the ρSTQ ranging ±0.25 to 0.5 nΩm in the transverse direction with width of 10 to 20 mm extending about 360 mm in the longitudinal direction. In a rough estimation, this fluctuation in ρ is corresponding to variation in Mg, Si or Cu contents of ±0.05 to 0.15 mass% from analysed compositions, though the species of alloying elements is not clear." @default.
- W599677788 created "2016-06-24" @default.
- W599677788 creator A5012316943 @default.
- W599677788 creator A5024297935 @default.
- W599677788 creator A5031502941 @default.
- W599677788 creator A5062230326 @default.
- W599677788 creator A5064670069 @default.
- W599677788 date "2005-01-01" @default.
- W599677788 modified "2023-10-18" @default.
- W599677788 title "Continuous resistivity fluctuation of rolled Al-Mg-Si-Cu alloy sheets" @default.
- W599677788 cites W1973756216 @default.
- W599677788 cites W1974172770 @default.
- W599677788 cites W1975692454 @default.
- W599677788 cites W2005790170 @default.
- W599677788 cites W2007168894 @default.
- W599677788 cites W2016787377 @default.
- W599677788 cites W2514417900 @default.
- W599677788 doi "https://doi.org/10.2464/jilm.55.125" @default.
- W599677788 hasPublicationYear "2005" @default.
- W599677788 type Work @default.
- W599677788 sameAs 599677788 @default.
- W599677788 citedByCount "8" @default.
- W599677788 crossrefType "journal-article" @default.
- W599677788 hasAuthorship W599677788A5012316943 @default.
- W599677788 hasAuthorship W599677788A5024297935 @default.
- W599677788 hasAuthorship W599677788A5031502941 @default.
- W599677788 hasAuthorship W599677788A5062230326 @default.
- W599677788 hasAuthorship W599677788A5064670069 @default.
- W599677788 hasBestOaLocation W5996777881 @default.
- W599677788 hasConcept C113196181 @default.
- W599677788 hasConcept C119599485 @default.
- W599677788 hasConcept C127413603 @default.
- W599677788 hasConcept C159985019 @default.
- W599677788 hasConcept C185592680 @default.
- W599677788 hasConcept C191897082 @default.
- W599677788 hasConcept C192562407 @default.
- W599677788 hasConcept C2779227376 @default.
- W599677788 hasConcept C2780026712 @default.
- W599677788 hasConcept C43617362 @default.
- W599677788 hasConcept C44255700 @default.
- W599677788 hasConcept C69990965 @default.
- W599677788 hasConceptScore W599677788C113196181 @default.
- W599677788 hasConceptScore W599677788C119599485 @default.
- W599677788 hasConceptScore W599677788C127413603 @default.
- W599677788 hasConceptScore W599677788C159985019 @default.
- W599677788 hasConceptScore W599677788C185592680 @default.
- W599677788 hasConceptScore W599677788C191897082 @default.
- W599677788 hasConceptScore W599677788C192562407 @default.
- W599677788 hasConceptScore W599677788C2779227376 @default.
- W599677788 hasConceptScore W599677788C2780026712 @default.
- W599677788 hasConceptScore W599677788C43617362 @default.
- W599677788 hasConceptScore W599677788C44255700 @default.
- W599677788 hasConceptScore W599677788C69990965 @default.
- W599677788 hasIssue "3" @default.
- W599677788 hasLocation W5996777881 @default.
- W599677788 hasOpenAccess W599677788 @default.
- W599677788 hasPrimaryLocation W5996777881 @default.
- W599677788 hasRelatedWork W1527876827 @default.
- W599677788 hasRelatedWork W1980659072 @default.
- W599677788 hasRelatedWork W1999962534 @default.
- W599677788 hasRelatedWork W2004457068 @default.
- W599677788 hasRelatedWork W2036094944 @default.
- W599677788 hasRelatedWork W2333845068 @default.
- W599677788 hasRelatedWork W2372376965 @default.
- W599677788 hasRelatedWork W2994278106 @default.
- W599677788 hasRelatedWork W3110113505 @default.
- W599677788 hasRelatedWork W4285097618 @default.
- W599677788 hasVolume "55" @default.
- W599677788 isParatext "false" @default.
- W599677788 isRetracted "false" @default.
- W599677788 magId "599677788" @default.
- W599677788 workType "article" @default.