- W60099229 abstract "This thesis is concerned with in-situ time-, temperature- and pressure-resolved synchrotron X-ray powder diffraction investigations of a variety of inorganic compounds with twodimensional layer structures and three-dimensional framework structures. In particular, phase stability, reaction kinetics, thermal expansion and compressibility at non-ambient conditions has been studied for 1) Phosphates with composition MIV(HPO4)2·nH2O (MIV = Ti, Zr); 2) Pyrophosphates and pyrovanadates with composition MIVX2O7 (MIV = Ti, Zr and X = P, V); 3) Molybdates with composition ZrMo2O8. The results are compiled in seven published papers and two manuscripts.Reaction kinetics for the hydrothermal synthesis of α-Ti(HPO4)2·H2O and intercalation of alkane diamines in α-Zr(HPO4)2·H2O was studied using time-resolved experiments. In the high-temperature transformation of γ-Ti(PO4)(H2PO4)·2H2O to TiP2O7 three intermediate phases, γ'-Ti(PO4)(H2PO4)·(2-x)H2O, β-Ti(PO4)(H2PO4) and Ti(PO4)(H2P2O7)0.5 were found to crystallise at 323, 373 and 748 K, respectively. A new tetragonal three-dimensional phosphate phase called τ-Zr(HPO4)2 was prepared, and subsequently its structure was determined and refined using the Rietveld method. In the high-temperature transformation from τ-Zr(HPO4)2 to cubic α-ZrP2O7 two new orthorhombic intermediate phases were found. The first intermediate phase, ρ-Zr(HPO4)2, forms at 598 K, and the second phase, β-ZrP2O7, at 688 K. Their respective structures were solved using direct methods and refined using the Rietveld method. In-situ high-pressure studies of τ-Zr(HPO4)2 revealed two new phases, tetragonal ν-Zr(HPO4)2 and orthorhombic ω-Zr(HPO4)2 that crystallise at 1.1 and 8.2 GPa. The structure of ν-Zr(HPO4)2 was solved and refined using the Rietveld method.The high-pressure properties of the pyrophosphates ZrP2O7 and TiP2O7, and the pyrovanadate ZrV2O7 were studied up to 40 GPa. Both pyrophosphates display smooth compression up to the highest pressures, while ZrV2O7 has a phase transformation at 1.38 GPa from cubic to pseudo-tetragonal β-ZrV2O7 and becomes X-ray amorphous at pressures above 4 GPa.In-situ high-pressure studies of trigonal α-ZrMo2O8 revealed the existence of two new phases, monoclinic δ-ZrMo2O8 and triclinic e-ZrMo2O8 that crystallises at 1.1 and 2.5 GPa, respectively. The structure of δ-ZrMo2O8 was solved by direct methods and refined using the Rietveld method." @default.
- W60099229 created "2016-06-24" @default.
- W60099229 creator A5026252670 @default.
- W60099229 creator A5045686649 @default.
- W60099229 creator A5055853844 @default.
- W60099229 date "2004-01-01" @default.
- W60099229 modified "2023-09-27" @default.
- W60099229 title "In-Situ Time-Resolved Synchrotron X-ray Powder Diffraction Studies of Hydrothermal Synthesis of Layered Titanium Phosphates." @default.
- W60099229 hasPublicationYear "2004" @default.
- W60099229 type Work @default.
- W60099229 sameAs 60099229 @default.
- W60099229 citedByCount "0" @default.
- W60099229 crossrefType "journal-article" @default.
- W60099229 hasAuthorship W60099229A5026252670 @default.
- W60099229 hasAuthorship W60099229A5045686649 @default.
- W60099229 hasAuthorship W60099229A5055853844 @default.
- W60099229 hasConcept C115624301 @default.
- W60099229 hasConcept C115645028 @default.
- W60099229 hasConcept C120665830 @default.
- W60099229 hasConcept C121332964 @default.
- W60099229 hasConcept C127413603 @default.
- W60099229 hasConcept C156622251 @default.
- W60099229 hasConcept C170751736 @default.
- W60099229 hasConcept C178790620 @default.
- W60099229 hasConcept C185039092 @default.
- W60099229 hasConcept C185592680 @default.
- W60099229 hasConcept C191897082 @default.
- W60099229 hasConcept C192562407 @default.
- W60099229 hasConcept C207114421 @default.
- W60099229 hasConcept C2776871784 @default.
- W60099229 hasConcept C37243968 @default.
- W60099229 hasConcept C42360764 @default.
- W60099229 hasConcept C44280652 @default.
- W60099229 hasConcept C50515024 @default.
- W60099229 hasConcept C506065880 @default.
- W60099229 hasConcept C8010536 @default.
- W60099229 hasConceptScore W60099229C115624301 @default.
- W60099229 hasConceptScore W60099229C115645028 @default.
- W60099229 hasConceptScore W60099229C120665830 @default.
- W60099229 hasConceptScore W60099229C121332964 @default.
- W60099229 hasConceptScore W60099229C127413603 @default.
- W60099229 hasConceptScore W60099229C156622251 @default.
- W60099229 hasConceptScore W60099229C170751736 @default.
- W60099229 hasConceptScore W60099229C178790620 @default.
- W60099229 hasConceptScore W60099229C185039092 @default.
- W60099229 hasConceptScore W60099229C185592680 @default.
- W60099229 hasConceptScore W60099229C191897082 @default.
- W60099229 hasConceptScore W60099229C192562407 @default.
- W60099229 hasConceptScore W60099229C207114421 @default.
- W60099229 hasConceptScore W60099229C2776871784 @default.
- W60099229 hasConceptScore W60099229C37243968 @default.
- W60099229 hasConceptScore W60099229C42360764 @default.
- W60099229 hasConceptScore W60099229C44280652 @default.
- W60099229 hasConceptScore W60099229C50515024 @default.
- W60099229 hasConceptScore W60099229C506065880 @default.
- W60099229 hasConceptScore W60099229C8010536 @default.
- W60099229 hasLocation W600992291 @default.
- W60099229 hasOpenAccess W60099229 @default.
- W60099229 hasPrimaryLocation W600992291 @default.
- W60099229 hasRelatedWork W1489350415 @default.
- W60099229 hasRelatedWork W1974115490 @default.
- W60099229 hasRelatedWork W1992553273 @default.
- W60099229 hasRelatedWork W2006763770 @default.
- W60099229 hasRelatedWork W2008015102 @default.
- W60099229 hasRelatedWork W2019315039 @default.
- W60099229 hasRelatedWork W2039020935 @default.
- W60099229 hasRelatedWork W2048502714 @default.
- W60099229 hasRelatedWork W2051470616 @default.
- W60099229 hasRelatedWork W2061452881 @default.
- W60099229 hasRelatedWork W2066798862 @default.
- W60099229 hasRelatedWork W2088422763 @default.
- W60099229 hasRelatedWork W2088868078 @default.
- W60099229 hasRelatedWork W2137259984 @default.
- W60099229 hasRelatedWork W2159362988 @default.
- W60099229 hasRelatedWork W2624840950 @default.
- W60099229 hasRelatedWork W2809342296 @default.
- W60099229 hasRelatedWork W2950676046 @default.
- W60099229 hasRelatedWork W2951202588 @default.
- W60099229 hasRelatedWork W2951252750 @default.
- W60099229 isParatext "false" @default.
- W60099229 isRetracted "false" @default.
- W60099229 magId "60099229" @default.
- W60099229 workType "article" @default.