- W62033902 abstract "The net adsorption test (NAT) (M-001) developed for the SUPERPAVE mix design procedure is of interest to those concerned with selecting binders and chippings for chip seals (surface dressings). The relevance of the NAT, which is performed on the fine aggregate fraction, for assessing the adhesion performance of chipping sizes of 14 mm (0.55 in.) used for chip seals and the behavior of bitumen emulsions is evaluated. Since the surface chemical composition of 14-mm (0.55-in.) chippings was not found to be statistically different from the composition of the fine aggregate fraction from the crushed chippings, it was accepted that NAT results were indicative of the adhesion performance of the chippings with the binder used in the test. In testing bitumen emulsions the prior removal of the water phase by evaporation was necessary. Results obtained with aggregate-bitumen combinations used for chip sealing in Ireland corresponded to the Strategic Highway Research Program (SHRP) findings that aggregate type has a dominating influence on binder-aggregate adhesion. However, with aggregate-emulsion combinations the emulsion source had a major effect, and the influence and type of emulsion surfactant was assumed to be responsible for the very specific affinity of these binders for aggregates. This is consistent with results of SHRP studies on the effect of antistripping agents on bonding energies. If the percentage net adsorption is determined on the basis of the total binder in the test solution, an overall expression of the binder-aggregate affinity and resistance to moisture damage is provided." @default.
- W62033902 created "2016-06-24" @default.
- W62033902 creator A5037645878 @default.
- W62033902 creator A5041080682 @default.
- W62033902 creator A5084092076 @default.
- W62033902 date "1995-01-01" @default.
- W62033902 modified "2023-09-24" @default.
- W62033902 title "NET ADSORPTION TEST FOR CHIP-SEALING AGGREGATES AND BINDERS" @default.
- W62033902 cites W650885763 @default.
- W62033902 hasPublicationYear "1995" @default.
- W62033902 type Work @default.
- W62033902 sameAs 62033902 @default.
- W62033902 citedByCount "2" @default.
- W62033902 crossrefType "journal-article" @default.
- W62033902 hasAuthorship W62033902A5037645878 @default.
- W62033902 hasAuthorship W62033902A5041080682 @default.
- W62033902 hasAuthorship W62033902A5084092076 @default.
- W62033902 hasConcept C127413603 @default.
- W62033902 hasConcept C149629883 @default.
- W62033902 hasConcept C150394285 @default.
- W62033902 hasConcept C159985019 @default.
- W62033902 hasConcept C168056786 @default.
- W62033902 hasConcept C178790620 @default.
- W62033902 hasConcept C185592680 @default.
- W62033902 hasConcept C192562407 @default.
- W62033902 hasConcept C2778123984 @default.
- W62033902 hasConcept C2779227376 @default.
- W62033902 hasConcept C2986189917 @default.
- W62033902 hasConcept C42360764 @default.
- W62033902 hasConcept C43617362 @default.
- W62033902 hasConcept C4679612 @default.
- W62033902 hasConcept C548081761 @default.
- W62033902 hasConcept C68928338 @default.
- W62033902 hasConceptScore W62033902C127413603 @default.
- W62033902 hasConceptScore W62033902C149629883 @default.
- W62033902 hasConceptScore W62033902C150394285 @default.
- W62033902 hasConceptScore W62033902C159985019 @default.
- W62033902 hasConceptScore W62033902C168056786 @default.
- W62033902 hasConceptScore W62033902C178790620 @default.
- W62033902 hasConceptScore W62033902C185592680 @default.
- W62033902 hasConceptScore W62033902C192562407 @default.
- W62033902 hasConceptScore W62033902C2778123984 @default.
- W62033902 hasConceptScore W62033902C2779227376 @default.
- W62033902 hasConceptScore W62033902C2986189917 @default.
- W62033902 hasConceptScore W62033902C42360764 @default.
- W62033902 hasConceptScore W62033902C43617362 @default.
- W62033902 hasConceptScore W62033902C4679612 @default.
- W62033902 hasConceptScore W62033902C548081761 @default.
- W62033902 hasConceptScore W62033902C68928338 @default.
- W62033902 hasIssue "1507" @default.
- W62033902 hasLocation W620339021 @default.
- W62033902 hasOpenAccess W62033902 @default.
- W62033902 hasPrimaryLocation W620339021 @default.
- W62033902 hasRelatedWork W133676539 @default.
- W62033902 hasRelatedWork W1502226326 @default.
- W62033902 hasRelatedWork W1545413693 @default.
- W62033902 hasRelatedWork W16592066 @default.
- W62033902 hasRelatedWork W1785818880 @default.
- W62033902 hasRelatedWork W1966400441 @default.
- W62033902 hasRelatedWork W201135867 @default.
- W62033902 hasRelatedWork W2071348804 @default.
- W62033902 hasRelatedWork W2088211649 @default.
- W62033902 hasRelatedWork W2218923789 @default.
- W62033902 hasRelatedWork W2240492838 @default.
- W62033902 hasRelatedWork W2283875837 @default.
- W62033902 hasRelatedWork W22913324 @default.
- W62033902 hasRelatedWork W2954618110 @default.
- W62033902 hasRelatedWork W566540366 @default.
- W62033902 hasRelatedWork W586590573 @default.
- W62033902 hasRelatedWork W647805170 @default.
- W62033902 hasRelatedWork W650741088 @default.
- W62033902 hasRelatedWork W748355729 @default.
- W62033902 hasRelatedWork W848623728 @default.
- W62033902 isParatext "false" @default.
- W62033902 isRetracted "false" @default.
- W62033902 magId "62033902" @default.
- W62033902 workType "article" @default.