- W6450994 abstract "In the present project, (Ba0.9Ca0.1)(Ti1-xSnx)O3(x=0.06, 0.08 and 0.1) lead-free ceramics were synthesized by conventional solid state route. XRD analysis of calcined sample shows formation of perovskite phase. The BZT- BCT ceramic samples were calcined and sintered at lower temperatures 1300oC and 1350oC, respectively which was lower compared to the previous reported literature. The average particle size was found to be 0.5-1μm from FESEM analysis. Dielectric measurements of the sintered sample were carried out for the compositions over the frequency range of 42 Hz -1MHz and temperature range from 28oC to 100oC. Each sample showed a maximum dielectric constant at the Curie temperature (TC). With increase in the value of ‗x‘ from 0.06 to 0.1 the composition had shown decrease in the Curie temperature values which were 85oC, 40oC and 30oC respectively. The dielectric and piezoelectric properties of our sintered samples are comparable to those of conventionally prepared (Ba0.9Ca0.1)(Ti1-xSnx)O3 ceramics reported earlier. These ceramics are potential candidates for the lead-free piezoelectric applications." @default.
- W6450994 created "2016-06-24" @default.
- W6450994 creator A5029302824 @default.
- W6450994 date "2014-01-01" @default.
- W6450994 modified "2023-09-27" @default.
- W6450994 title "Dielectric and Piezoelectric Properties of lead free ferroelectric (Ba0.9Ca0.1)(Ti1-xSnx)O3(x=0.06, 0.08,0.1) Ceramics" @default.
- W6450994 hasPublicationYear "2014" @default.
- W6450994 type Work @default.
- W6450994 sameAs 6450994 @default.
- W6450994 citedByCount "0" @default.
- W6450994 crossrefType "dissertation" @default.
- W6450994 hasAuthorship W6450994A5029302824 @default.
- W6450994 hasConcept C100082104 @default.
- W6450994 hasConcept C113196181 @default.
- W6450994 hasConcept C121332964 @default.
- W6450994 hasConcept C133386390 @default.
- W6450994 hasConcept C134132462 @default.
- W6450994 hasConcept C155011858 @default.
- W6450994 hasConcept C159985019 @default.
- W6450994 hasConcept C161790260 @default.
- W6450994 hasConcept C178790620 @default.
- W6450994 hasConcept C185592680 @default.
- W6450994 hasConcept C192191005 @default.
- W6450994 hasConcept C192562407 @default.
- W6450994 hasConcept C199289684 @default.
- W6450994 hasConcept C26873012 @default.
- W6450994 hasConcept C2777949652 @default.
- W6450994 hasConcept C39353612 @default.
- W6450994 hasConcept C43617362 @default.
- W6450994 hasConcept C44280652 @default.
- W6450994 hasConcept C49040817 @default.
- W6450994 hasConcept C55493867 @default.
- W6450994 hasConcept C63648874 @default.
- W6450994 hasConcept C7082614 @default.
- W6450994 hasConcept C79090758 @default.
- W6450994 hasConcept C8010536 @default.
- W6450994 hasConcept C82217956 @default.
- W6450994 hasConcept C97355855 @default.
- W6450994 hasConceptScore W6450994C100082104 @default.
- W6450994 hasConceptScore W6450994C113196181 @default.
- W6450994 hasConceptScore W6450994C121332964 @default.
- W6450994 hasConceptScore W6450994C133386390 @default.
- W6450994 hasConceptScore W6450994C134132462 @default.
- W6450994 hasConceptScore W6450994C155011858 @default.
- W6450994 hasConceptScore W6450994C159985019 @default.
- W6450994 hasConceptScore W6450994C161790260 @default.
- W6450994 hasConceptScore W6450994C178790620 @default.
- W6450994 hasConceptScore W6450994C185592680 @default.
- W6450994 hasConceptScore W6450994C192191005 @default.
- W6450994 hasConceptScore W6450994C192562407 @default.
- W6450994 hasConceptScore W6450994C199289684 @default.
- W6450994 hasConceptScore W6450994C26873012 @default.
- W6450994 hasConceptScore W6450994C2777949652 @default.
- W6450994 hasConceptScore W6450994C39353612 @default.
- W6450994 hasConceptScore W6450994C43617362 @default.
- W6450994 hasConceptScore W6450994C44280652 @default.
- W6450994 hasConceptScore W6450994C49040817 @default.
- W6450994 hasConceptScore W6450994C55493867 @default.
- W6450994 hasConceptScore W6450994C63648874 @default.
- W6450994 hasConceptScore W6450994C7082614 @default.
- W6450994 hasConceptScore W6450994C79090758 @default.
- W6450994 hasConceptScore W6450994C8010536 @default.
- W6450994 hasConceptScore W6450994C82217956 @default.
- W6450994 hasConceptScore W6450994C97355855 @default.
- W6450994 hasLocation W64509941 @default.
- W6450994 hasOpenAccess W6450994 @default.
- W6450994 hasPrimaryLocation W64509941 @default.
- W6450994 hasRelatedWork W1228141911 @default.
- W6450994 hasRelatedWork W1484680597 @default.
- W6450994 hasRelatedWork W1964419276 @default.
- W6450994 hasRelatedWork W1973153068 @default.
- W6450994 hasRelatedWork W1988476093 @default.
- W6450994 hasRelatedWork W1992295588 @default.
- W6450994 hasRelatedWork W2023329635 @default.
- W6450994 hasRelatedWork W2035763923 @default.
- W6450994 hasRelatedWork W2050694855 @default.
- W6450994 hasRelatedWork W2063933423 @default.
- W6450994 hasRelatedWork W2072851639 @default.
- W6450994 hasRelatedWork W2121182147 @default.
- W6450994 hasRelatedWork W2183134874 @default.
- W6450994 hasRelatedWork W2217521157 @default.
- W6450994 hasRelatedWork W2244499769 @default.
- W6450994 hasRelatedWork W2249980981 @default.
- W6450994 hasRelatedWork W2387487231 @default.
- W6450994 hasRelatedWork W2608068522 @default.
- W6450994 hasRelatedWork W2070874 @default.
- W6450994 hasRelatedWork W2523027710 @default.
- W6450994 isParatext "false" @default.
- W6450994 isRetracted "false" @default.
- W6450994 magId "6450994" @default.
- W6450994 workType "dissertation" @default.