- W647559117 abstract "THE KINDS OF CALCIUM SILICATE HYDRATES FORMED DURING AUTOCLAVING ARE IDENTIFIED AND THEIR EFFECTS DETERMINED ON THE MECHANICAL STRENGTH OR OTHER PROPERTIES OF THE AUTOCLAVED TEST SPECIMENS. FROM THE RESULTS OF THESE TESTS, BINDING CAPACITIES OF SEVERAL HYDRATE COMPOUNDS, AS WELL AS SUITABLE CONDITIONS FOR AUTOCLAVE CURING OF CEMENTS, ARE DISCUSSED. THREE CEMENTS, ORDINARY PORTLAND CEMENT /OPC/, PORTLAND BLAST-FURNACE SLAG CEMENT /PBC/ AND SPECIALLY PREPARED CEMENT /SMC/ WERE USED IN THIS STUDY. OPC AND PBC WERE OF PLANT MANUFACTURE. THE CONTENT OF BLAST-FURNACE SLAG IN PBC WAS 45 PERCENT BY WEIGHT. SMC WAS PREPARED BY MIXING 60 PERCENT OPC AND 40 PERCENT SILICEOUS ROCK POWDER BY WEIGHT. THE PROPERTIES OF EACH CEMENT ARE INDICATED IN TABLES. CEMENT PASTES WERE MADE AT WATER-CEMENT RATIO OF 0.30, MIXED FOR 3 MIN, AND MOLDED INTO 4X4X16-CM PRISMS. AFTER 1 DAY MOIST CURING AT ROOM TEMPERATURE /20C, 98 PERCENT RH/, THE PRISMS WERE REMOVED FROM THE MOLDS AND IMMEDIATELY PLACED IN AN AUTOCLAVE. FOUR CURING TEMPERATURES AND VAPOR PRESSURES WERE USED IN FIVE AUTOCLAVE CURING PERIODS. THE TIME NEEDED FOR TEMPERATURE RISE IN THE AUTOCLAVE AND THE TIME NEEDED FOR COOLING IT DOWN TO ROOM TEMPERATURE WERE ALWAYS KEPT CONSTANT /ABOUT 2.5 HR/. THREE PRISMS WERE PREPARED FOR EXAMINATION AT EACH CURING CONDITION. SPECIMENS FOR CHEMICAL ANALYSIS WERE PREPARED BY GRINDING THE HARDENED PRISMS FINELY AND DRYING TO CONSTANT WEIGHT AT 105-110 C. IT WAS DETERMINED THAT THE COMPRESSIVE STRENGTH OF HARDENED PASTE CURED BY AUTOCLAVING DEPENDS ON TEMPERATURE, PRESSURE AND DURATION OF CURING. NO RELATIONSHIP IS RECOGNIZED BETWEEN FLEXURAL AND COMPRESSIVE STRENGTHS IN THE HARDENED PRISMS OF OPC AND PBC, BUT THERE IS A FAILRY LINEAR RELATIONSHIP BETWEEN THEM IN THE HARDENED PRISMS OF SMC. THE AMOUNTS OF IGNITION LOSS AND FREE CA/OH/2 IN CURED PRISMS OF OPC AND PBC SHOW A TENDENCY TO DECREASE WITH RISE OF CURING TEMPERATURE AND PRESSURE. ACCORDING TO X-RAY IDENTIFICATION, THE HYDRATION PRODUCTS ARE MAINLY CALCIUM SILICATE HYDRATES AND FREE CA/OH/2. SMC IS CONSIDERED TO BE THE CEMENT MOST SUITED FOR AUTOCLAVE CURING." @default.
- W647559117 created "2016-06-24" @default.
- W647559117 creator A5072031201 @default.
- W647559117 creator A5079648111 @default.
- W647559117 date "1966-01-01" @default.
- W647559117 modified "2023-09-24" @default.
- W647559117 title "STRENGTH AND MICROSTRUCTURES OF HARDENED CEMENT PASTES CURED BY AUTOCLAVING" @default.
- W647559117 hasPublicationYear "1966" @default.
- W647559117 type Work @default.
- W647559117 sameAs 647559117 @default.
- W647559117 citedByCount "0" @default.
- W647559117 crossrefType "journal-article" @default.
- W647559117 hasAuthorship W647559117A5072031201 @default.
- W647559117 hasAuthorship W647559117A5079648111 @default.
- W647559117 hasConcept C132976073 @default.
- W647559117 hasConcept C159985019 @default.
- W647559117 hasConcept C191897082 @default.
- W647559117 hasConcept C192562407 @default.
- W647559117 hasConcept C2779850335 @default.
- W647559117 hasConcept C2780021121 @default.
- W647559117 hasConcept C30407753 @default.
- W647559117 hasConcept C33819350 @default.
- W647559117 hasConcept C43088074 @default.
- W647559117 hasConcept C523993062 @default.
- W647559117 hasConcept C87976508 @default.
- W647559117 hasConceptScore W647559117C132976073 @default.
- W647559117 hasConceptScore W647559117C159985019 @default.
- W647559117 hasConceptScore W647559117C191897082 @default.
- W647559117 hasConceptScore W647559117C192562407 @default.
- W647559117 hasConceptScore W647559117C2779850335 @default.
- W647559117 hasConceptScore W647559117C2780021121 @default.
- W647559117 hasConceptScore W647559117C30407753 @default.
- W647559117 hasConceptScore W647559117C33819350 @default.
- W647559117 hasConceptScore W647559117C43088074 @default.
- W647559117 hasConceptScore W647559117C523993062 @default.
- W647559117 hasConceptScore W647559117C87976508 @default.
- W647559117 hasIssue "90" @default.
- W647559117 hasLocation W6475591171 @default.
- W647559117 hasOpenAccess W647559117 @default.
- W647559117 hasPrimaryLocation W6475591171 @default.
- W647559117 hasRelatedWork W1039773792 @default.
- W647559117 hasRelatedWork W1569582963 @default.
- W647559117 hasRelatedWork W1954803009 @default.
- W647559117 hasRelatedWork W1988651307 @default.
- W647559117 hasRelatedWork W1997741348 @default.
- W647559117 hasRelatedWork W2024041083 @default.
- W647559117 hasRelatedWork W2049599946 @default.
- W647559117 hasRelatedWork W2291837599 @default.
- W647559117 hasRelatedWork W2293687581 @default.
- W647559117 hasRelatedWork W2331354198 @default.
- W647559117 hasRelatedWork W2372792154 @default.
- W647559117 hasRelatedWork W2605555222 @default.
- W647559117 hasRelatedWork W2731456529 @default.
- W647559117 hasRelatedWork W2767929164 @default.
- W647559117 hasRelatedWork W2803562890 @default.
- W647559117 hasRelatedWork W2890309758 @default.
- W647559117 hasRelatedWork W2999741503 @default.
- W647559117 hasRelatedWork W3152018183 @default.
- W647559117 hasRelatedWork W2512364851 @default.
- W647559117 hasRelatedWork W2847891895 @default.
- W647559117 isParatext "false" @default.
- W647559117 isRetracted "false" @default.
- W647559117 magId "647559117" @default.
- W647559117 workType "article" @default.