- W71587278 abstract "A study was made of the oxidation resistince of ten high-temperature alloys: (I) aluminum-modified Nichrome V, (2) Nichrome V, (3) niobium-modlfied Nichrome V, (4) am iron-chromium-aluminum alloy, (5) Inconel 702, (6) Hastelloy R235, F) Hastelloy W, (8) type 316 stainless steel, (9) Inconel X, and (10) In conel. Tests included the measurement of the average depth of external oxidation and raaximum depth of oxide penetration on specimens that had been subjected to stress in air at hlgh temperature for 100 hours, and on specimens that had been subjected to stress in air under fluctuating-temperature conditions for an equlvalent length of time, plus continuous recording of the weight change of specimens oxidized in air at high temperatures. The depth of oxidation was found to increase with temperature and wlth stress. There was little effect of stress at stresses below that required toproduce 1% extension in 100 hours. All of the alloys conformed reasonably well to the parabolic rate law in the welghtgain oxidation tests. (auth)" @default.
- W71587278 created "2016-06-24" @default.
- W71587278 creator A5032193485 @default.
- W71587278 creator A5069859698 @default.
- W71587278 date "1958-05-27" @default.
- W71587278 modified "2023-09-26" @default.
- W71587278 title "OXIDATION OF EXPERIMENTAL ALLOYS. Period covered: March 1, 1956 to November 30, 1957" @default.
- W71587278 hasPublicationYear "1958" @default.
- W71587278 type Work @default.
- W71587278 sameAs 71587278 @default.
- W71587278 citedByCount "0" @default.
- W71587278 crossrefType "journal-article" @default.
- W71587278 hasAuthorship W71587278A5032193485 @default.
- W71587278 hasAuthorship W71587278A5069859698 @default.
- W71587278 hasConcept C140086010 @default.
- W71587278 hasConcept C191897082 @default.
- W71587278 hasConcept C192562407 @default.
- W71587278 hasConcept C2778703219 @default.
- W71587278 hasConcept C2779851234 @default.
- W71587278 hasConcept C2780026712 @default.
- W71587278 hasConcept C507968137 @default.
- W71587278 hasConcept C511782168 @default.
- W71587278 hasConcept C513153333 @default.
- W71587278 hasConceptScore W71587278C140086010 @default.
- W71587278 hasConceptScore W71587278C191897082 @default.
- W71587278 hasConceptScore W71587278C192562407 @default.
- W71587278 hasConceptScore W71587278C2778703219 @default.
- W71587278 hasConceptScore W71587278C2779851234 @default.
- W71587278 hasConceptScore W71587278C2780026712 @default.
- W71587278 hasConceptScore W71587278C507968137 @default.
- W71587278 hasConceptScore W71587278C511782168 @default.
- W71587278 hasConceptScore W71587278C513153333 @default.
- W71587278 hasLocation W715872781 @default.
- W71587278 hasOpenAccess W71587278 @default.
- W71587278 hasPrimaryLocation W715872781 @default.
- W71587278 hasRelatedWork W1981375265 @default.
- W71587278 hasRelatedWork W1987336723 @default.
- W71587278 hasRelatedWork W2020568858 @default.
- W71587278 hasRelatedWork W2026564040 @default.
- W71587278 hasRelatedWork W2322167902 @default.
- W71587278 hasRelatedWork W2325779075 @default.
- W71587278 hasRelatedWork W2329864271 @default.
- W71587278 hasRelatedWork W2334789103 @default.
- W71587278 hasRelatedWork W2559820755 @default.
- W71587278 hasRelatedWork W2794355740 @default.
- W71587278 hasRelatedWork W2983518413 @default.
- W71587278 hasRelatedWork W3139612109 @default.
- W71587278 hasRelatedWork W1526234485 @default.
- W71587278 hasRelatedWork W2260596777 @default.
- W71587278 hasRelatedWork W2302405667 @default.
- W71587278 hasRelatedWork W2816852386 @default.
- W71587278 hasRelatedWork W2830811840 @default.
- W71587278 hasRelatedWork W2846371960 @default.
- W71587278 hasRelatedWork W3103268812 @default.
- W71587278 hasRelatedWork W3144477831 @default.
- W71587278 isParatext "false" @default.
- W71587278 isRetracted "false" @default.
- W71587278 magId "71587278" @default.
- W71587278 workType "article" @default.