• W744437791 abstract "CrN/TiN multilayer coatings were deposited by pulsed dc magnetron sputtering (PDCMS) in a closed field unbalanced magnetron sputtering system. The Ti target power was maintained at 2000 W while the Cr target power was varied from 70 to 1000 W. As the Cr target power was increased, CrN/TiN multilayer coatings with the Cr/(Cr + Ti) ratio of 0.037–0.573 had a single phase face-centered cubic structure with a texture evolution from (111) to (220). The residual stress of the coatings increased from − 1.03 GPa to − 5.65 GPa. The hardness and the H/E* and H3/E*2 ratios of the coatings exhibited an initial increase with the increasing Cr target power, then followed by a decrease. The coating with a Cr/(Cr + Ti) ratio of 0.30 reached the highest hardness and the H/E* and H3/E*2 ratios of 31 GPa, 0.0832 and 0.214, respectively. The coating also showed a dominant oxidative wear with the lowest friction coefficient and specific wear rate of 0.41 and 2.3 × 10− 6 mm3 N− 1 m− 1, respectively. The increase in the H/E* and H3/E*2 ratios led to the increase in the toughness and cohesion/adhesion strength of the coatings with the increased HF levels and critical loads (LC1, LC2 and LC3). However, the coatings with similar H/E* and H3/E*2 ratios exhibited different tribological properties due to the different critical loads LC3 resulted from the increased compressive residual stress. The improvements in toughness and cohesion/adhesion strength promoted the reduction in the crack initiation and propagation, and oxidative wear during dry sliding tests." @default.
• W744437791 created "2016-06-24" @default.
• W744437791 creator A5002129758 @default.
• W744437791 creator A5003643142 @default.
• W744437791 creator A5020961753 @default.
• W744437791 creator A5021197484 @default.
• W744437791 creator A5053196661 @default.
• W744437791 creator A5068788351 @default.
• W744437791 date "2015-08-01" @default.
• W744437791 modified "2023-10-16" @default.
• W744437791 title "Mechanical and tribological properties of CrN/TiN multilayer coatings deposited by pulsed dc magnetron sputtering" @default.
• W744437791 cites W1497736951 @default.
• W744437791 cites W1573264325 @default.
• W744437791 cites W1966541960 @default.
• W744437791 cites W1972789570 @default.
• W744437791 cites W1974165582 @default.
• W744437791 cites W1974844569 @default.
• W744437791 cites W1976850538 @default.
• W744437791 cites W1979753997 @default.
• W744437791 cites W1981966175 @default.
• W744437791 cites W1990351237 @default.
• W744437791 cites W1991325436 @default.
• W744437791 cites W1994818243 @default.
• W744437791 cites W1998674449 @default.
• W744437791 cites W2002468578 @default.
• W744437791 cites W2011344579 @default.
• W744437791 cites W2011718688 @default.
• W744437791 cites W2012010093 @default.
• W744437791 cites W2015857270 @default.
• W744437791 cites W2019034741 @default.
• W744437791 cites W2022958224 @default.
• W744437791 cites W2023053552 @default.
• W744437791 cites W2023382426 @default.
• W744437791 cites W2028208869 @default.
• W744437791 cites W2029850737 @default.
• W744437791 cites W2030572513 @default.
• W744437791 cites W2032768349 @default.
• W744437791 cites W2039758910 @default.
• W744437791 cites W2043503912 @default.
• W744437791 cites W2044859455 @default.
• W744437791 cites W2049105457 @default.
• W744437791 cites W2049959659 @default.
• W744437791 cites W2055761626 @default.
• W744437791 cites W2057414384 @default.
• W744437791 cites W2059022607 @default.
• W744437791 cites W2060284346 @default.
• W744437791 cites W2068308658 @default.
• W744437791 cites W2070052387 @default.
• W744437791 cites W2071142872 @default.
• W744437791 cites W2083301226 @default.
• W744437791 cites W2084181397 @default.
• W744437791 cites W2090817495 @default.
• W744437791 cites W2092079086 @default.
• W744437791 cites W2095787778 @default.
• W744437791 cites W2110508635 @default.
• W744437791 cites W2131558742 @default.
• W744437791 cites W2132946984 @default.
• W744437791 cites W2166880727 @default.
• W744437791 cites W4362174777 @default.
• W744437791 doi "https://doi.org/10.1016/j.surfcoat.2015.06.064" @default.
• W744437791 hasPublicationYear "2015" @default.
• W744437791 type Work @default.
• W744437791 sameAs 744437791 @default.
• W744437791 citedByCount "52" @default.
• W744437791 countsByYear W7444377912015 @default.
• W744437791 countsByYear W7444377912016 @default.
• W744437791 countsByYear W7444377912017 @default.
• W744437791 countsByYear W7444377912018 @default.
• W744437791 countsByYear W7444377912019 @default.
• W744437791 countsByYear W7444377912020 @default.
• W744437791 countsByYear W7444377912021 @default.
• W744437791 countsByYear W7444377912022 @default.
• W744437791 countsByYear W7444377912023 @default.
• W744437791 crossrefType "journal-article" @default.
• W744437791 hasAuthorship W744437791A5002129758 @default.
• W744437791 hasAuthorship W744437791A5003643142 @default.
• W744437791 hasAuthorship W744437791A5020961753 @default.
• W744437791 hasAuthorship W744437791A5021197484 @default.
• W744437791 hasAuthorship W744437791A5053196661 @default.
• W744437791 hasAuthorship W744437791A5068788351 @default.
• W744437791 hasConcept C123408415 @default.
• W744437791 hasConcept C159985019 @default.
• W744437791 hasConcept C167310744 @default.
• W744437791 hasConcept C171250308 @default.
• W744437791 hasConcept C19067145 @default.
• W744437791 hasConcept C191897082 @default.
• W744437791 hasConcept C192562407 @default.
• W744437791 hasConcept C22423302 @default.
• W744437791 hasConcept C2781083372 @default.
• W744437791 hasConcept C2781448156 @default.
• W744437791 hasConcept C37292000 @default.
• W744437791 hasConcept C525849907 @default.
• W744437791 hasConcept C61427134 @default.
• W744437791 hasConcept C97892325 @default.
• W744437791 hasConceptScore W744437791C123408415 @default.
• W744437791 hasConceptScore W744437791C159985019 @default.
• W744437791 hasConceptScore W744437791C167310744 @default.
• W744437791 hasConceptScore W744437791C171250308 @default.

• next