- W808173554 endingPage "888" @default.
- W808173554 startingPage "879" @default.
- W808173554 abstract "The effects of final annealing temperature on the microstructure and creep characteristics were investigated for the Zr-lNb-0.2X (X=0, Mo, Cu) and Zr-lNb- 1Sn-0.3Fe-0.1X (X=0, Mo, Cu) alloys. The microstructures were observed by using TEM/EDS, and grain size and distributions of precipitates were analyzed using a image analyzer. The creep test was performed at under applied stress of 150 MPa for 10 days. The -Zr was observed at annealing temperature above . In the temperature above, the grain sizes of both alloy systems appeared to be increased with increasing the final annealing temperature. The creep strengths of Zr-1Nb-1Sn-0.3Fe-0.1X alloys were higher than those of Zr-1Nb-0.2X ones due to the effect of solid solution hardening by Sn in Zr-lNb-lSn-0.3Fe-0.1X alloy system. Also, Mo addition showed the strong effect of precipitate hardening in both alloy systems. The creep strength rapidly decreased with increasing the annealing temperature up to . However, a superior creep resistance was obtained in the sample that annealed to have a second phase of -Zr. It was considered that the appearance of -Zr would play an important role in the strengthening mechanism of creep deformation." @default.
- W808173554 created "2016-06-24" @default.
- W808173554 creator A5004864569 @default.
- W808173554 creator A5013878168 @default.
- W808173554 creator A5016296144 @default.
- W808173554 creator A5030399794 @default.
- W808173554 creator A5067411233 @default.
- W808173554 creator A5072481277 @default.
- W808173554 creator A5072956994 @default.
- W808173554 creator A5078931878 @default.
- W808173554 creator A5086382334 @default.
- W808173554 creator A5089996595 @default.
- W808173554 date "2001-01-01" @default.
- W808173554 modified "2023-09-24" @default.
- W808173554 title "Effect of Final Annealing Temperature on Microstructure and Creep Characteristics of Nb-containing Zirconium Alloys" @default.
- W808173554 hasPublicationYear "2001" @default.
- W808173554 type Work @default.
- W808173554 sameAs 808173554 @default.
- W808173554 citedByCount "0" @default.
- W808173554 crossrefType "journal-article" @default.
- W808173554 hasAuthorship W808173554A5004864569 @default.
- W808173554 hasAuthorship W808173554A5013878168 @default.
- W808173554 hasAuthorship W808173554A5016296144 @default.
- W808173554 hasAuthorship W808173554A5030399794 @default.
- W808173554 hasAuthorship W808173554A5067411233 @default.
- W808173554 hasAuthorship W808173554A5072481277 @default.
- W808173554 hasAuthorship W808173554A5072956994 @default.
- W808173554 hasAuthorship W808173554A5078931878 @default.
- W808173554 hasAuthorship W808173554A5086382334 @default.
- W808173554 hasAuthorship W808173554A5089996595 @default.
- W808173554 hasConcept C149912024 @default.
- W808173554 hasConcept C154634170 @default.
- W808173554 hasConcept C159985019 @default.
- W808173554 hasConcept C191897082 @default.
- W808173554 hasConcept C192562407 @default.
- W808173554 hasConcept C2777855556 @default.
- W808173554 hasConcept C2779227376 @default.
- W808173554 hasConcept C2780026712 @default.
- W808173554 hasConcept C34425451 @default.
- W808173554 hasConcept C44255700 @default.
- W808173554 hasConcept C534791751 @default.
- W808173554 hasConcept C87976508 @default.
- W808173554 hasConceptScore W808173554C149912024 @default.
- W808173554 hasConceptScore W808173554C154634170 @default.
- W808173554 hasConceptScore W808173554C159985019 @default.
- W808173554 hasConceptScore W808173554C191897082 @default.
- W808173554 hasConceptScore W808173554C192562407 @default.
- W808173554 hasConceptScore W808173554C2777855556 @default.
- W808173554 hasConceptScore W808173554C2779227376 @default.
- W808173554 hasConceptScore W808173554C2780026712 @default.
- W808173554 hasConceptScore W808173554C34425451 @default.
- W808173554 hasConceptScore W808173554C44255700 @default.
- W808173554 hasConceptScore W808173554C534791751 @default.
- W808173554 hasConceptScore W808173554C87976508 @default.
- W808173554 hasIssue "10" @default.
- W808173554 hasLocation W8081735541 @default.
- W808173554 hasOpenAccess W808173554 @default.
- W808173554 hasPrimaryLocation W8081735541 @default.
- W808173554 hasRelatedWork W1981793357 @default.
- W808173554 hasRelatedWork W1994132138 @default.
- W808173554 hasRelatedWork W1995406072 @default.
- W808173554 hasRelatedWork W2008261240 @default.
- W808173554 hasRelatedWork W2014267758 @default.
- W808173554 hasRelatedWork W2019719784 @default.
- W808173554 hasRelatedWork W2041650010 @default.
- W808173554 hasRelatedWork W2048692228 @default.
- W808173554 hasRelatedWork W2090660700 @default.
- W808173554 hasRelatedWork W2524547137 @default.
- W808173554 hasRelatedWork W2751026941 @default.
- W808173554 hasRelatedWork W2770214287 @default.
- W808173554 hasRelatedWork W2911702557 @default.
- W808173554 hasRelatedWork W2920595021 @default.
- W808173554 hasRelatedWork W3048312788 @default.
- W808173554 hasRelatedWork W3091898859 @default.
- W808173554 hasRelatedWork W3119685702 @default.
- W808173554 hasRelatedWork W3197416139 @default.
- W808173554 hasRelatedWork W805786734 @default.
- W808173554 hasRelatedWork W2491480022 @default.
- W808173554 hasVolume "11" @default.
- W808173554 isParatext "false" @default.
- W808173554 isRetracted "false" @default.
- W808173554 magId "808173554" @default.
- W808173554 workType "article" @default.