- W826315428 endingPage "438" @default.
- W826315428 startingPage "433" @default.
- W826315428 abstract "The thermal fluidity and injection moldability of oven-dry steam-treated bamboo powder were investigated with control of the temperature. Thermal analysis, such as differential thermal analysis and thermogravimetry, indicated that the steamed powder underwent degradation at lower temperatures, and the weight loss of the steamed powder was larger than that for the untreated powder. Thermal flow tests of the steamed powder at several temperatures revealed the flow rate was high at 180 and 200 °C. Injection molding was attempted while controlling the temperature of the injection part and metal mold. It was possible to obtain products with a surface similar to plastic via injection molding and the range of metal mold temperature that resulted in a successfully molded product increased with the injection temperature. The four-point bending strength and Rockwell superficial hardness of the product increased with the mold temperature at each injection temperature. Both characteristics were high when the injection temperature was 180 °C, and the highest values obtained were 36 MPa and HR15w 78. Observation of the fracture part of the molded product confirmed that the fiber strength of the product molded at an injection temperature of 180 °C was maintained, while that molded at an injection temperature of 200 °C was not." @default.
- W826315428 created "2016-06-24" @default.
- W826315428 creator A5024216161 @default.
- W826315428 creator A5032923985 @default.
- W826315428 date "2015-11-01" @default.
- W826315428 modified "2023-09-24" @default.
- W826315428 title "Effect of molding temperature on fluidity and injection moldability of oven-dry steam-treated bamboo powder" @default.
- W826315428 cites W1545218050 @default.
- W826315428 cites W1970288613 @default.
- W826315428 cites W1992622296 @default.
- W826315428 cites W2029106461 @default.
- W826315428 cites W2055653364 @default.
- W826315428 cites W2056451767 @default.
- W826315428 cites W2070779004 @default.
- W826315428 cites W2086240520 @default.
- W826315428 cites W2321269562 @default.
- W826315428 doi "https://doi.org/10.1016/j.jmatprotec.2015.05.015" @default.
- W826315428 hasPublicationYear "2015" @default.
- W826315428 type Work @default.
- W826315428 sameAs 826315428 @default.
- W826315428 citedByCount "8" @default.
- W826315428 countsByYear W8263154282015 @default.
- W826315428 countsByYear W8263154282017 @default.
- W826315428 countsByYear W8263154282020 @default.
- W826315428 countsByYear W8263154282021 @default.
- W826315428 countsByYear W8263154282022 @default.
- W826315428 crossrefType "journal-article" @default.
- W826315428 hasAuthorship W826315428A5024216161 @default.
- W826315428 hasAuthorship W826315428A5032923985 @default.
- W826315428 hasConcept C121332964 @default.
- W826315428 hasConcept C153294291 @default.
- W826315428 hasConcept C159985019 @default.
- W826315428 hasConcept C192562407 @default.
- W826315428 hasConcept C2777216800 @default.
- W826315428 hasConcept C2777581544 @default.
- W826315428 hasConcept C2778993590 @default.
- W826315428 hasConcept C2780566776 @default.
- W826315428 hasConcept C39353612 @default.
- W826315428 hasConcept C67558686 @default.
- W826315428 hasConceptScore W826315428C121332964 @default.
- W826315428 hasConceptScore W826315428C153294291 @default.
- W826315428 hasConceptScore W826315428C159985019 @default.
- W826315428 hasConceptScore W826315428C192562407 @default.
- W826315428 hasConceptScore W826315428C2777216800 @default.
- W826315428 hasConceptScore W826315428C2777581544 @default.
- W826315428 hasConceptScore W826315428C2778993590 @default.
- W826315428 hasConceptScore W826315428C2780566776 @default.
- W826315428 hasConceptScore W826315428C39353612 @default.
- W826315428 hasConceptScore W826315428C67558686 @default.
- W826315428 hasLocation W8263154281 @default.
- W826315428 hasOpenAccess W826315428 @default.
- W826315428 hasPrimaryLocation W8263154281 @default.
- W826315428 hasRelatedWork W1994820608 @default.
- W826315428 hasRelatedWork W2004123151 @default.
- W826315428 hasRelatedWork W2023846961 @default.
- W826315428 hasRelatedWork W2101533454 @default.
- W826315428 hasRelatedWork W2513282232 @default.
- W826315428 hasRelatedWork W2674333698 @default.
- W826315428 hasRelatedWork W2718291857 @default.
- W826315428 hasRelatedWork W4236619181 @default.
- W826315428 hasRelatedWork W4240544601 @default.
- W826315428 hasRelatedWork W587319886 @default.
- W826315428 hasVolume "225" @default.
- W826315428 isParatext "false" @default.
- W826315428 isRetracted "false" @default.
- W826315428 magId "826315428" @default.
- W826315428 workType "article" @default.