- W830421133 abstract "The purpose of this study was to observe shear bond strength of composite resin to dentin following surface treatment. Freshly extracted forty-eight sound human molars were used in this study. They were stored at physiologic saline solution before experiment. The teeth was then mounted with self curing acrylic resin in brass mold. The buccal surfaces of the teeth were grinding approximately 1.5mm by means of water-irrigated grinding wheel to expose the flattened fresh dentin surfaces. The specimens were divided into 6 groups according to preparation and treatment procedures on dentin surfaces; Group 1: Untreated after preparation with No.301 diamond point Group 2: Treated with primer for 60 seconds after preparation with No.301 diamond point Group 3: Untreated after preparation with No.700 fissure carbide bur Group 4: Treated with primer for 60 seconds after preparation with No.700 fissure carbide bur Group 5: Untreated after grinding with 600 grit silicon carbide paper Group 6: Treated with primer for 60 seconds after grinding with 600 grit silicon carbide paper Light cure dental adhesive was applicated to each specimen. Silux plus(3M) was inserted then into polyethylene tube of 3mm diameter and 3mm height, and polymerized to dentin surface. All of the specimens were stored in distilled water at for 24 hours prior to testing. The shear bond strength was measured using an Instron Universal Testing Machine. The results obtained from this study were as follows: 1. The shear bond strength to dentin was the highest in group II. 2. The shear bond strength to dentin was the lowest in group III. 3. There was no significant difference in shear bond strength to dentin according to preparation instrument. 4. The primer treatment group showed significantly greater shear bond strength than untreated group." @default.
- W830421133 created "2016-06-24" @default.
- W830421133 creator A5031352734 @default.
- W830421133 creator A5080371456 @default.
- W830421133 date "1991-01-01" @default.
- W830421133 modified "2023-09-23" @default.
- W830421133 title "A STUDY ON SHEAR BOND STRENGTH OF COMPOSITE RESIN TO DENTIN FOLLOWING SURFACE TREATMENTS" @default.
- W830421133 hasPublicationYear "1991" @default.
- W830421133 type Work @default.
- W830421133 sameAs 830421133 @default.
- W830421133 citedByCount "0" @default.
- W830421133 crossrefType "journal-article" @default.
- W830421133 hasAuthorship W830421133A5031352734 @default.
- W830421133 hasAuthorship W830421133A5080371456 @default.
- W830421133 hasConcept C104779481 @default.
- W830421133 hasConcept C112950240 @default.
- W830421133 hasConcept C140013486 @default.
- W830421133 hasConcept C156887251 @default.
- W830421133 hasConcept C159096172 @default.
- W830421133 hasConcept C159985019 @default.
- W830421133 hasConcept C180478085 @default.
- W830421133 hasConcept C185592680 @default.
- W830421133 hasConcept C192562407 @default.
- W830421133 hasConcept C199343813 @default.
- W830421133 hasConcept C202271784 @default.
- W830421133 hasConcept C2777571299 @default.
- W830421133 hasConcept C2778265030 @default.
- W830421133 hasConcept C2779227376 @default.
- W830421133 hasConcept C2779263046 @default.
- W830421133 hasConcept C2779429693 @default.
- W830421133 hasConcept C2781448156 @default.
- W830421133 hasConcept C43617362 @default.
- W830421133 hasConcept C68928338 @default.
- W830421133 hasConcept C71924100 @default.
- W830421133 hasConceptScore W830421133C104779481 @default.
- W830421133 hasConceptScore W830421133C112950240 @default.
- W830421133 hasConceptScore W830421133C140013486 @default.
- W830421133 hasConceptScore W830421133C156887251 @default.
- W830421133 hasConceptScore W830421133C159096172 @default.
- W830421133 hasConceptScore W830421133C159985019 @default.
- W830421133 hasConceptScore W830421133C180478085 @default.
- W830421133 hasConceptScore W830421133C185592680 @default.
- W830421133 hasConceptScore W830421133C192562407 @default.
- W830421133 hasConceptScore W830421133C199343813 @default.
- W830421133 hasConceptScore W830421133C202271784 @default.
- W830421133 hasConceptScore W830421133C2777571299 @default.
- W830421133 hasConceptScore W830421133C2778265030 @default.
- W830421133 hasConceptScore W830421133C2779227376 @default.
- W830421133 hasConceptScore W830421133C2779263046 @default.
- W830421133 hasConceptScore W830421133C2779429693 @default.
- W830421133 hasConceptScore W830421133C2781448156 @default.
- W830421133 hasConceptScore W830421133C43617362 @default.
- W830421133 hasConceptScore W830421133C68928338 @default.
- W830421133 hasConceptScore W830421133C71924100 @default.
- W830421133 hasIssue "1" @default.
- W830421133 hasLocation W8304211331 @default.
- W830421133 hasOpenAccess W830421133 @default.
- W830421133 hasPrimaryLocation W8304211331 @default.
- W830421133 hasRelatedWork W134005168 @default.
- W830421133 hasRelatedWork W1533938263 @default.
- W830421133 hasRelatedWork W1589170017 @default.
- W830421133 hasRelatedWork W171106867 @default.
- W830421133 hasRelatedWork W1781719160 @default.
- W830421133 hasRelatedWork W2229375237 @default.
- W830421133 hasRelatedWork W2294928157 @default.
- W830421133 hasRelatedWork W2401963958 @default.
- W830421133 hasRelatedWork W2411255705 @default.
- W830421133 hasRelatedWork W2415111574 @default.
- W830421133 hasRelatedWork W2440782355 @default.
- W830421133 hasRelatedWork W2475347656 @default.
- W830421133 hasRelatedWork W46436822 @default.
- W830421133 hasRelatedWork W636244518 @default.
- W830421133 hasRelatedWork W801100196 @default.
- W830421133 hasRelatedWork W832002878 @default.
- W830421133 hasRelatedWork W84546033 @default.
- W830421133 hasRelatedWork W853701158 @default.
- W830421133 hasRelatedWork W861251156 @default.
- W830421133 hasRelatedWork W924943573 @default.
- W830421133 hasVolume "16" @default.
- W830421133 isParatext "false" @default.
- W830421133 isRetracted "false" @default.
- W830421133 magId "830421133" @default.
- W830421133 workType "article" @default.