- W856935146 abstract "The relationship between the microstructure of alumina scales, adhesion, and sulfur content was examined through a series of nickel alloys oxidized in 1100 to 1200 deg. C cyclic or isothermal exposures in air. In cyclic tests of undoped NiCrAl, adhesion was produced when the sulfur content was reduced, without any change in scale microstructure. Although interfacial voids were not observed in cyclic tests of NiCrAl, they were promoted by long-term isothermal exposures, by sulfur doping, and in most exposures of NiAl. Two single crystal superalloys, PWA 1480 and Rene' N5, were also tested, either in the as-received condition or after the sulfur content had been reduced to less than 1 ppmw by hydrogen annealing. The unannealed alloys always exhibited spalling to bare metal, but interfacial voids were not observed consistently. Desulfurized PWA 1480 and Rene' N5 exhibited remarkable adhesion and no voidage for either isothermal or cyclic exposures. The most consistent microstructural feature was that, for the cases where voids did form, the scale undersides exhibited corresponding areas with ridged oxide grain boundaries. Voids were not required for spallation nor were other microstructural features essential for adhesion. These observations are consistent with the model whereby scale spallation is controlled primarily by interfacial sulfur segregation and the consequent degradation of oxide-metal bonding." @default.
- W856935146 created "2016-06-24" @default.
- W856935146 creator A5043942109 @default.
- W856935146 date "1997-03-01" @default.
- W856935146 modified "2023-09-24" @default.
- W856935146 title "Sulfur Impurities and the Microstructure of Alumina Scales" @default.
- W856935146 cites W1964697149 @default.
- W856935146 cites W1967640448 @default.
- W856935146 cites W1972336097 @default.
- W856935146 cites W1975343793 @default.
- W856935146 cites W1980917373 @default.
- W856935146 cites W2019974415 @default.
- W856935146 cites W2029590465 @default.
- W856935146 cites W2029832716 @default.
- W856935146 cites W2039643984 @default.
- W856935146 cites W2051145855 @default.
- W856935146 cites W2053099646 @default.
- W856935146 cites W2065704018 @default.
- W856935146 cites W2066446425 @default.
- W856935146 cites W2070524619 @default.
- W856935146 cites W2080945497 @default.
- W856935146 cites W2081537086 @default.
- W856935146 cites W2087268552 @default.
- W856935146 cites W2092776010 @default.
- W856935146 cites W2111674737 @default.
- W856935146 cites W2163792511 @default.
- W856935146 cites W279764956 @default.
- W856935146 cites W1502045165 @default.
- W856935146 cites W2051133618 @default.
- W856935146 hasPublicationYear "1997" @default.
- W856935146 type Work @default.
- W856935146 sameAs 856935146 @default.
- W856935146 citedByCount "0" @default.
- W856935146 crossrefType "journal-article" @default.
- W856935146 hasAuthorship W856935146A5043942109 @default.
- W856935146 hasConcept C11608111 @default.
- W856935146 hasConcept C121332964 @default.
- W856935146 hasConcept C133347239 @default.
- W856935146 hasConcept C152568617 @default.
- W856935146 hasConcept C159985019 @default.
- W856935146 hasConcept C191897082 @default.
- W856935146 hasConcept C192562407 @default.
- W856935146 hasConcept C207055975 @default.
- W856935146 hasConcept C2779851234 @default.
- W856935146 hasConcept C518881349 @default.
- W856935146 hasConcept C62520636 @default.
- W856935146 hasConcept C87976508 @default.
- W856935146 hasConcept C97355855 @default.
- W856935146 hasConceptScore W856935146C11608111 @default.
- W856935146 hasConceptScore W856935146C121332964 @default.
- W856935146 hasConceptScore W856935146C133347239 @default.
- W856935146 hasConceptScore W856935146C152568617 @default.
- W856935146 hasConceptScore W856935146C159985019 @default.
- W856935146 hasConceptScore W856935146C191897082 @default.
- W856935146 hasConceptScore W856935146C192562407 @default.
- W856935146 hasConceptScore W856935146C207055975 @default.
- W856935146 hasConceptScore W856935146C2779851234 @default.
- W856935146 hasConceptScore W856935146C518881349 @default.
- W856935146 hasConceptScore W856935146C62520636 @default.
- W856935146 hasConceptScore W856935146C87976508 @default.
- W856935146 hasConceptScore W856935146C97355855 @default.
- W856935146 hasLocation W8569351461 @default.
- W856935146 hasOpenAccess W856935146 @default.
- W856935146 hasPrimaryLocation W8569351461 @default.
- W856935146 hasRelatedWork W1129172065 @default.
- W856935146 hasRelatedWork W1974838519 @default.
- W856935146 hasRelatedWork W1979938848 @default.
- W856935146 hasRelatedWork W1995478246 @default.
- W856935146 hasRelatedWork W2032501515 @default.
- W856935146 hasRelatedWork W2056584150 @default.
- W856935146 hasRelatedWork W2061525350 @default.
- W856935146 hasRelatedWork W2069197585 @default.
- W856935146 hasRelatedWork W2084856772 @default.
- W856935146 hasRelatedWork W2270271291 @default.
- W856935146 hasRelatedWork W2323849345 @default.
- W856935146 hasRelatedWork W2368322189 @default.
- W856935146 hasRelatedWork W2460357606 @default.
- W856935146 hasRelatedWork W263522845 @default.
- W856935146 hasRelatedWork W2752520810 @default.
- W856935146 hasRelatedWork W2972465505 @default.
- W856935146 hasRelatedWork W3001039166 @default.
- W856935146 hasRelatedWork W3171617963 @default.
- W856935146 hasRelatedWork W3176895216 @default.
- W856935146 hasRelatedWork W817002707 @default.
- W856935146 isParatext "false" @default.
- W856935146 isRetracted "false" @default.
- W856935146 magId "856935146" @default.
- W856935146 workType "article" @default.