- W86403748 abstract "Annealing beta-heat-treated production-size dingoturanium core blanks in the high alpha range (1150 to 1200 deg F) produced a fine, equiaxed grain size by a recrystallization process. The extent of recrystallization is dependent upon the rate of cooling through the beta-to-alpha transformation, the time and temperature of annealing, and whether or not impurities that retard grain growth are present. The cooling rate through the beta-to-alpha transformation was varied by using a range of beta temperatures and air cooling times prior to quenching into water. Longer air cooling times are permissible at the higher beta temperatures; however, the greatest amount of induced lattice strain was obtained after an air delay of only 2 seconds before quenching. Decreasing the annealing temperature results in a corresponding increase in the annealing time required for an equivalent amount of recrystallization. A second phase, present in the alloyed dingot metal, inhibited recrystallization and grain growth. Alloyed metal recrystallized progressively from the outer periphery to the center of the core, whereas unalloyed metal subjected to identical annealing conditions exhibited recrystallized grains throughout the cross section. A reduction in grain size from 0.38 mm to 0.25 mm occurred in a beta-treated, unalloyed core after annealing at 1200 deg F for 4 hours. The grain size of betaquenched, alloyed metal decreased from 0.28 mm to 0.19 mm on recrystallization. There appears to be change in the orientation of a beta-quenched core as a result of recrystallization. The beta quench-alpha anneal process could be integrated with an alpha-phase vacuum outgassing process to produce fine-grained metal that is essentially free of strain and preferred orientation and has a low hydrogen c ontent. (auth)" @default.
- W86403748 created "2016-06-24" @default.
- W86403748 creator A5042581081 @default.
- W86403748 creator A5064249925 @default.
- W86403748 date "1962-08-24" @default.
- W86403748 modified "2023-09-27" @default.
- W86403748 title "RECRYSTALLIZATION OF BETA-HEAT-TREATED DINGOT-URANIUM CORES. Topical Report" @default.
- W86403748 doi "https://doi.org/10.2172/4792031" @default.
- W86403748 hasPublicationYear "1962" @default.
- W86403748 type Work @default.
- W86403748 sameAs 86403748 @default.
- W86403748 citedByCount "0" @default.
- W86403748 crossrefType "report" @default.
- W86403748 hasAuthorship W86403748A5042581081 @default.
- W86403748 hasAuthorship W86403748A5064249925 @default.
- W86403748 hasBestOaLocation W864037483 @default.
- W86403748 hasConcept C151730666 @default.
- W86403748 hasConcept C191897082 @default.
- W86403748 hasConcept C192191005 @default.
- W86403748 hasConcept C192562407 @default.
- W86403748 hasConcept C195702682 @default.
- W86403748 hasConcept C2777855556 @default.
- W86403748 hasConcept C81710450 @default.
- W86403748 hasConcept C86803240 @default.
- W86403748 hasConcept C87976508 @default.
- W86403748 hasConcept C98390173 @default.
- W86403748 hasConceptScore W86403748C151730666 @default.
- W86403748 hasConceptScore W86403748C191897082 @default.
- W86403748 hasConceptScore W86403748C192191005 @default.
- W86403748 hasConceptScore W86403748C192562407 @default.
- W86403748 hasConceptScore W86403748C195702682 @default.
- W86403748 hasConceptScore W86403748C2777855556 @default.
- W86403748 hasConceptScore W86403748C81710450 @default.
- W86403748 hasConceptScore W86403748C86803240 @default.
- W86403748 hasConceptScore W86403748C87976508 @default.
- W86403748 hasConceptScore W86403748C98390173 @default.
- W86403748 hasLocation W864037481 @default.
- W86403748 hasLocation W864037482 @default.
- W86403748 hasLocation W864037483 @default.
- W86403748 hasLocation W864037484 @default.
- W86403748 hasOpenAccess W86403748 @default.
- W86403748 hasPrimaryLocation W864037481 @default.
- W86403748 hasRelatedWork W2027044219 @default.
- W86403748 hasRelatedWork W2059615866 @default.
- W86403748 hasRelatedWork W2086175172 @default.
- W86403748 hasRelatedWork W2349400266 @default.
- W86403748 hasRelatedWork W2368151789 @default.
- W86403748 hasRelatedWork W2393478015 @default.
- W86403748 hasRelatedWork W248779315 @default.
- W86403748 hasRelatedWork W2995480550 @default.
- W86403748 hasRelatedWork W3194014449 @default.
- W86403748 hasRelatedWork W3212116301 @default.
- W86403748 isParatext "false" @default.
- W86403748 isRetracted "false" @default.
- W86403748 magId "86403748" @default.
- W86403748 workType "report" @default.