- W96285614 abstract "Objective: To assess in vitro the bond strength of a machined surface of a Au-Ti alloy to a veneering ceramic. Method and Materials: Metal strips of the alloy Au 1.7-Ti 0.1-Ir were milled from a semiproduct fabricated by continuous casting and cold forming. For comparison, the same alloy as well as a traditional Au-Pt-Pd-In alloy were used in the as-cast state. Six samples of each group were fabricated for the crack initiation test, according to ISO 9693:1999, by preparing appropriate metal strips that were veneered with ceramic using a standard firing procedure. The crack initiation test was performed in a universal testing machine. Load at fracture was recorded. Means of bond strength were calculated for each group and the results compared by use of a 1-sided Student t test (P < .05). Fracture sites were documented by means of SEM. Results: Bond strength in the 3 groups was in the same order of magnitude. Failure mode was different for both alloys. Failure of the bonding to the Au-Ti alloy predominantly occurred at the alloy-oxide interface, no matter which fabrication process was used. On the Au-Pt-Pd-In alloy, more ceramic residues were observed. Conclusion: The machined alloy Au 1.7-Ti 0.1-Ir provides sufficient bond strength to veneering ceramics, but this has to be proven by a clinical study. (Quintessence Int 2007;38:867-872)." @default.
- W96285614 created "2016-06-24" @default.
- W96285614 creator A5007776675 @default.
- W96285614 creator A5074380755 @default.
- W96285614 date "2007-11-01" @default.
- W96285614 modified "2023-09-23" @default.
- W96285614 title "Ceramic bonding to a machined Au-Ti alloy." @default.
- W96285614 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/18197327" @default.
- W96285614 hasPublicationYear "2007" @default.
- W96285614 type Work @default.
- W96285614 sameAs 96285614 @default.
- W96285614 citedByCount "0" @default.
- W96285614 crossrefType "journal-article" @default.
- W96285614 hasAuthorship W96285614A5007776675 @default.
- W96285614 hasAuthorship W96285614A5074380755 @default.
- W96285614 hasConcept C112950240 @default.
- W96285614 hasConcept C134132462 @default.
- W96285614 hasConcept C136525101 @default.
- W96285614 hasConcept C142724271 @default.
- W96285614 hasConcept C159096172 @default.
- W96285614 hasConcept C159985019 @default.
- W96285614 hasConcept C16635281 @default.
- W96285614 hasConcept C180478085 @default.
- W96285614 hasConcept C191897082 @default.
- W96285614 hasConcept C192562407 @default.
- W96285614 hasConcept C204787440 @default.
- W96285614 hasConcept C2779227376 @default.
- W96285614 hasConcept C2779851234 @default.
- W96285614 hasConcept C2780026712 @default.
- W96285614 hasConcept C2984173401 @default.
- W96285614 hasConcept C43369102 @default.
- W96285614 hasConcept C68928338 @default.
- W96285614 hasConcept C71924100 @default.
- W96285614 hasConceptScore W96285614C112950240 @default.
- W96285614 hasConceptScore W96285614C134132462 @default.
- W96285614 hasConceptScore W96285614C136525101 @default.
- W96285614 hasConceptScore W96285614C142724271 @default.
- W96285614 hasConceptScore W96285614C159096172 @default.
- W96285614 hasConceptScore W96285614C159985019 @default.
- W96285614 hasConceptScore W96285614C16635281 @default.
- W96285614 hasConceptScore W96285614C180478085 @default.
- W96285614 hasConceptScore W96285614C191897082 @default.
- W96285614 hasConceptScore W96285614C192562407 @default.
- W96285614 hasConceptScore W96285614C204787440 @default.
- W96285614 hasConceptScore W96285614C2779227376 @default.
- W96285614 hasConceptScore W96285614C2779851234 @default.
- W96285614 hasConceptScore W96285614C2780026712 @default.
- W96285614 hasConceptScore W96285614C2984173401 @default.
- W96285614 hasConceptScore W96285614C43369102 @default.
- W96285614 hasConceptScore W96285614C68928338 @default.
- W96285614 hasConceptScore W96285614C71924100 @default.
- W96285614 hasIssue "10" @default.
- W96285614 hasLocation W962856141 @default.
- W96285614 hasOpenAccess W96285614 @default.
- W96285614 hasPrimaryLocation W962856141 @default.
- W96285614 hasRelatedWork W1985770657 @default.
- W96285614 hasRelatedWork W2003246840 @default.
- W96285614 hasRelatedWork W2054530446 @default.
- W96285614 hasRelatedWork W2064015821 @default.
- W96285614 hasRelatedWork W2083221542 @default.
- W96285614 hasRelatedWork W2104677291 @default.
- W96285614 hasRelatedWork W2109774963 @default.
- W96285614 hasRelatedWork W2119018056 @default.
- W96285614 hasRelatedWork W2333331866 @default.
- W96285614 hasRelatedWork W2377379024 @default.
- W96285614 hasRelatedWork W2397049031 @default.
- W96285614 hasRelatedWork W2403165775 @default.
- W96285614 hasRelatedWork W2589706449 @default.
- W96285614 hasRelatedWork W27354858 @default.
- W96285614 hasRelatedWork W2746034733 @default.
- W96285614 hasRelatedWork W2776656389 @default.
- W96285614 hasRelatedWork W2782725092 @default.
- W96285614 hasRelatedWork W3029152391 @default.
- W96285614 hasRelatedWork W3031767434 @default.
- W96285614 hasRelatedWork W3111551501 @default.
- W96285614 hasVolume "38" @default.
- W96285614 isParatext "false" @default.
- W96285614 isRetracted "false" @default.
- W96285614 magId "96285614" @default.
- W96285614 workType "article" @default.