- W99577066 abstract "The compatibility of three strontium compounds (SrTiO3, Sr2TiO4, and SrO) with three superalloys (Haynes alloy No. 25, Hastelloy C, and Type 316 stainless steel) was studied at 900 and 1100°C for periods up to 10 000 h. The Sr2TiO4 was compatible under all test conditions, and only slight reaction occurred between SrTiO3 and the three superalloys. A 2- to 4-mil reaction zone developed between SrO and both Haynes alloy No. 25 and Hastelloy C at 900°C. At 1100°C the reaction was more extensive and also occurred with Type 316 stainless steel; however, the reaction rates became negligibly slow after 5000 h. For commercially produced Hastelloy C or C-276, the reaction with SrO appears to be related to the presence of one or more intermetallic phases. In laboratory heats containing very low silicon but relatively high carbon or in those containing very high silicon, these intermetallics did not form and no attack was observed.A reduction in the room-temperature mechanical properties of Haynes alloy No. 25, Hastelloy C, and Type 316 stainless steel was noted after heat treating at 900 or 1100°C. A further reduction in ductility was found in some of the samples exposed to SrO." @default.
- W99577066 created "2016-06-24" @default.
- W99577066 creator A5085974203 @default.
- W99577066 date "1973-02-01" @default.
- W99577066 modified "2023-09-23" @default.
- W99577066 title "Compatibility of Strontium Compounds with Superalloys at 900 and 1100°C" @default.
- W99577066 cites W2071991388 @default.
- W99577066 cites W2094372932 @default.
- W99577066 cites W4243129477 @default.
- W99577066 doi "https://doi.org/10.13182/nt73-a31239" @default.
- W99577066 hasPublicationYear "1973" @default.
- W99577066 type Work @default.
- W99577066 sameAs 99577066 @default.
- W99577066 citedByCount "1" @default.
- W99577066 crossrefType "journal-article" @default.
- W99577066 hasAuthorship W99577066A5085974203 @default.
- W99577066 hasConcept C178790620 @default.
- W99577066 hasConcept C185592680 @default.
- W99577066 hasConcept C191897082 @default.
- W99577066 hasConcept C192562407 @default.
- W99577066 hasConcept C207055975 @default.
- W99577066 hasConcept C27501479 @default.
- W99577066 hasConcept C2780026712 @default.
- W99577066 hasConcept C2781372787 @default.
- W99577066 hasConcept C518915863 @default.
- W99577066 hasConcept C544956773 @default.
- W99577066 hasConceptScore W99577066C178790620 @default.
- W99577066 hasConceptScore W99577066C185592680 @default.
- W99577066 hasConceptScore W99577066C191897082 @default.
- W99577066 hasConceptScore W99577066C192562407 @default.
- W99577066 hasConceptScore W99577066C207055975 @default.
- W99577066 hasConceptScore W99577066C27501479 @default.
- W99577066 hasConceptScore W99577066C2780026712 @default.
- W99577066 hasConceptScore W99577066C2781372787 @default.
- W99577066 hasConceptScore W99577066C518915863 @default.
- W99577066 hasConceptScore W99577066C544956773 @default.
- W99577066 hasIssue "2" @default.
- W99577066 hasLocation W995770661 @default.
- W99577066 hasOpenAccess W99577066 @default.
- W99577066 hasPrimaryLocation W995770661 @default.
- W99577066 hasRelatedWork W1007834781 @default.
- W99577066 hasRelatedWork W1999552040 @default.
- W99577066 hasRelatedWork W2089251307 @default.
- W99577066 hasRelatedWork W2099547899 @default.
- W99577066 hasRelatedWork W2471314110 @default.
- W99577066 hasRelatedWork W2608393618 @default.
- W99577066 hasRelatedWork W2766515653 @default.
- W99577066 hasRelatedWork W2894695206 @default.
- W99577066 hasRelatedWork W4250486179 @default.
- W99577066 hasRelatedWork W1979853529 @default.
- W99577066 hasVolume "17" @default.
- W99577066 isParatext "false" @default.
- W99577066 isRetracted "false" @default.
- W99577066 magId "99577066" @default.
- W99577066 workType "article" @default.